Glass compositions, fiberizable glass compositions, and glass fibers made therefrom

ABSTRACT

The present invention relates generally to glass compositions incorporating rare earth oxides (RE 2 O 3 ). In one embodiment, a glass composition suitable for fiber forming comprises 51-70 wt. % SiO 2 , 12.5-22 wt. % Al 2 O 3 , 0-20 wt. % CaO, 0-11 wt. % MgO, 0.2-1 wt. % Fe 2 O 3 , 0.05 or greater wt. % RE 2 O 3 , and greater than 1 wt. % MnO x . In another embodiment, a glass composition suitable for fiber forming comprises 51-70 wt. % SiO 2 , 12.5-22 wt. % Al 2 O 3 , 0-20 wt. % CaO, 0-11 wt. % MgO, 0.2-1 wt. % Fe 2 O 3 , 0.05 or greater wt. % RE 2 O 3 , 0-4 wt. % BaO, 0-4 wt. % SrO, and 0-5.5 wt. % ZnO, wherein the sum of BaO+SrO+ZnO is greater than about 2 wt. %. In another embodiment, a glass composition suitable for fiber forming comprises 51-70 wt. % SiO 2 , 12.5-22 wt. % Al 2 O 3 , 0-20 wt. % CaO, 0-11 wt. % MgO, 0.2-1 wt. % Fe 2 O 3 , 0.05 or greater wt. % RE 2 O 3 , and from greater than 0 to 2.5 wt. % Cu 2 O. In another embodiment, a glass composition suitable for fiber forming comprises 51-70 wt. % SiO 2 , 12.5-22 wt. % Al 2 O 3 , 0-20 wt. % CaO, 0-12.5 wt. % MgO, 0.2-1 wt. % Fe 2 O 3 , 0.05 or greater wt. % RE 2 O 3 , and at least one additional feature selected from the group consisting of: La 2 O 3  is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO 2 /Al 2 O 3  ratio greater than about 4. The glass compositions can be used to form glass fibers which can be incorporated into a variety of other fiber glass products (e.g., strands, rovings, fabrics, etc.) and incorporated into various composites.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. patent application Ser. No. 15/019,172, filed on Feb. 9, 2016, which is a continuation of U.S. patent application Ser. No. 14/325,854, filed on Jul. 8, 2014 and issued as U.S. Pat. No. 9,278,883 on Mar. 8, 2016, which claims priority to U.S. Provisional Patent Application Ser. No. 61/846,266, filed on Jul. 15, 2013, which are all hereby incorporated by reference as though fully set forth herein.

FIELD OF THE INVENTION

The present invention relates to glass compositions and, in particular, to glass compositions for forming fibers.

BACKGROUND OF THE INVENTION

Glass fibers have been used to reinforce various polymeric resins for many years. Some commonly used glass compositions for use in reinforcement applications include the “E-glass”, “R-glass”, and “D-glass” families of compositions. “S-glass” is another commonly used family of glass compositions that includes, for example, glass fibers commercially available from AGY (Aiken, S.C.) under the trade name “S-2 Glass.”

In reinforcement and other applications, certain mechanical properties of glass fibers or of composites reinforced with glass fibers can be important. However, in many instances, the manufacture of glass fibers having improved mechanical properties (e.g., higher strength, higher modulus, etc.) can result in higher costs due, for example, due to increased batch material costs, increased manufacturing costs, or other factors. For example, the aforementioned “S-2 Glass” has improved mechanical properties as compared to conventional E-glass but costs significantly more as well as a result of substantially higher temperature and energy demands for batch-to-glass conversion, melt fining, and fiber drawing. Fiber glass manufacturers continue to seek glass compositions that can be used to form glass fibers having desirable mechanical properties in a commercial manufacturing environment.

SUMMARY

Various embodiments of the present invention provide glass compositions, fiberizable glass compositions, and glass fibers formed from such compositions, as well as fiber glass strands, yarns, fabrics, and composites comprising such glass fibers adapted for use in various applications.

In one embodiment, a glass composition suitable for fiber forming comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). In some embodiments, MnO_(x) comprises MnO₂ in an amount of about 2 weight percent or greater. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises TiO₂ in an amount greater than about 3 weight percent. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

In another embodiment, a glass composition suitable for fiber forming comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments, BaO is present in an amount greater than about 2 weight percent. In some embodiments, SrO is present in an amount greater than about 2 weight percent. In some embodiments, ZnO is present in an amount greater than about 2 weight percent. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

In another embodiment, a glass composition suitable for fiber forming comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments, the composition comprises 0.5 weight percent or greater Cu₂O. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

In another embodiment, a glass composition suitable for fiber forming comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4. In some embodiments, the additional feature comprises La₂O₃ in an amount of about 3 weight percent or greater. In some embodiments, MgO is present in an amount greater than about 6 weight percent, and the additional feature comprises CaO in an amount less than about 1.5 weight percent. In some embodiments, the additional feature comprises the SiO₂/Al₂O₃ ratio in an amount greater than about 4.2. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

Some embodiments of the present invention relate to fiber glass strands. A number of fiberizable glass compositions are disclosed herein as part of the present invention, and it should be understand that various embodiments of the present invention can comprise glass fibers, fiber glass strands, yarns, and other products incorporating glass fibers formed from such compositions.

Some embodiments of the present invention relate to yarns formed from at least one fiber glass strand formed from a glass composition described herein. Some embodiments of the present invention relate to fabrics incorporating at least one fiber glass strand formed from a glass composition described herein. In some embodiments, a fill yarn used in the fabric can comprise the at least one fiber glass strand. A warp yarn, in some embodiments, can comprise the at least one fiber glass strand. In some embodiments, fiber glass strands can be used in both fill yarns and warp yarns used to form fabrics according to the present invention. In some embodiments, fabrics of the present invention can comprise a plain weave fabric, a twill fabric, a crowfoot fabric, a satin weave fabric, a stitch bonded fabric, or a 3D woven fabric.

Some embodiments of the present invention relate to composites comprising a polymeric resin and glass fibers formed from one of the various glass compositions described herein. The glass fibers can be from a fiber glass strand according to some embodiments of the present invention. In some embodiments, the glass fibers can be incorporated into a fabric, such as a woven fabric. For example, the glass fibers can be in a fill yarn and/or a warp yarn that are woven to form a fabric. In embodiments where the composite comprises a fabric, the fabric can comprise a plain weave fabric, a twill fabric, a crowfoot fabric, a satin weave fabric, a stitch bonded fabric, or a 3D woven fabric.

The glass fibers can be incorporated into the composite in other forms as well as discussed in more detail below.

With regard to polymeric resins, composites of the present invention can comprise one or more of a variety of polymeric resins. In some embodiments, the polymeric resin comprises at least one of polyethylene, polypropylene, polyamide, polyimide, polybutylene terephthalate, polycarbonate, thermoplastic polyurethane, phenolic, polyester, vinyl ester, polydicyclopentadiene, polyphenylene sulfide, polyether ether ketone, cyanate esters, bis-maleimides, and thermoset polyurethane resins. The polymeric resin can comprise an epoxy resin in some embodiments.

Composites of the present invention can be in a variety of forms and can be used in a variety of applications. Some examples of potential uses of composites according to some embodiments of the present invention include, without limitation, wind energy (e.g., windmill blades), automotive applications, safety/security applications (e.g., ballistics armor), aerospace or aviation applications (e.g., interior floors of planes), high pressure vessels or tanks, missile casings, electronics, and others.

These and other embodiments of the present invention are described in greater detail in the Detailed Description that follows.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a chart showing Young's modulus values relative to the amount of rare earth oxides (RE₂O₃) in various glass compositions.

FIG. 2 is a chart showing pristine fiber tensile strength values relative to the amount of rare earth oxides (RE₂O₃) in various glass compositions.

FIG. 3 is a chart showing softening and glass transition temperatures relative to the amount of rare earth oxides (RE₂O₃) in various glass compositions.

FIG. 4 is a chart showing linear coefficient of thermal expansion relative to the amount of scandium oxide (Sc₂O₃) in various glass compositions.

DETAILED DESCRIPTION

Unless indicated to the contrary, the numerical parameters set forth in the following specification are approximations that can vary depending upon the desired properties sought to be obtained by the present invention. At the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques.

Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contains certain errors necessarily resulting from the standard deviation found in their respective testing measurements. Moreover, all ranges disclosed herein are to be understood to encompass any and all subranges subsumed therein. For example, a stated range of “1 to 10” should be considered to include any and all subranges between (and inclusive of) the minimum value of 1 and the maximum value of 10; that is, all subranges beginning with a minimum value of 1 or more, e.g. 1 to 6.1, and ending with a maximum value of 10 or less, e.g., 5.5 to 10. Additionally, any reference referred to as being “incorporated herein” is to be understood as being incorporated in its entirety.

It is further noted that, as used in this specification, the singular forms “a,” “an,” and “the” include plural referents unless expressly and unequivocally limited to one referent.

The present invention relates generally to glass compositions. In one aspect, the present invention provides glass fibers formed from glass compositions described herein. In some embodiments, glass fibers of the present invention can have improved mechanical properties, such as, for example, Young's modulus and pristine strength, as compared to conventional E-glass fibers.

Glass compositions of the present invention comprise rare earth oxides in addition to components typically found in glass compositions such as SiO₂, Al₂O₃, CaO, MgO, and others. Such glass compositions can be fiberizable and thus can be used to make fiber glass in various embodiments. As used herein, the term “rare earth oxides” is abbreviated as “RE₂O₃” and, as understood to those of skill in the art, refers to oxides incorporating a rare earth metal and includes oxides of scandium (Sc₂O₃), yttrium (Y₂O₃), and the lanthanide elements (lanthanum (La₂O₃), cerium (Ce₂O₃ and CeO₂), praseodymium (Pr₂O₃), neodymium (Nd₂O₃), promethium (Pm₂O₃), samarium (Sm₂O₃), europium (Eu₂O₃ and EuO), gadolinium (Gd₂O₃), terbium (Tb₂O₃), dysprosium (Dy₂O₃), holmium (Ho₂O₃), erbium (Er₂O₃), thulium (Tm₂O₃), ytterbium (Yb₂O₃), and lutetium (Lu₂O₃)). The rare earth oxides are included in the glass compositions of the present invention in amounts that exceed those wherein the rare earth oxide is present only as a tramp material or impurity in a batch material included with a glass batch to provide another component. The glass compositions, in some embodiments, can comprise a combination of rare earth oxides (e.g., one or more of various rare earth oxides).

In some embodiments, one or more RE₂O₃ can be present in a glass composition in an amount of about 0.05 weight percent or greater. The one or more RE₂O₃ can be present in an amount of about 0.5 weight percent or greater in some embodiments. The one or more RE₂O₃ can be present in an amount of about 1 weight percent or greater in some embodiments. The one or more RE₂O₃ can be present in an amount of about 2 weight percent or greater in some embodiments. The one or more RE₂O₃ can be present in an amount of about 3 weight percent or greater in some embodiments. The one or more RE₂O₃ can be present in an amount of about 4 weight percent or greater in some embodiments. The one or more RE₂O₃ can be present in an amount of about 5 weight percent or greater in some embodiments. In some embodiments, the one or more RE₂O₃ can be present in an amount up to about 10 weight percent although greater amounts can be used in other embodiments. The one or more RE₂O₃, in some embodiments, can be present in an amount up to about 12 weight percent. The one or more RE₂O₃ can be present in an amount up to about 15 weight percent in some embodiments. The one or more RE₂O₃, in some embodiments, can be present in an amount from about 0.05 to about 15 weight percent. The one or more RE₂O₃ can be present in an amount from about 0.5 to about 15 weight percent in some embodiments. In some embodiments, the one or more RE₂O₃ can be present in an amount from about 2.0 to about 15 weight percent. The one or more RE₂O₃, in some embodiments, can be present in an amount from about 3.0 to about 15 weight percent. In some embodiments, the one or more RE₂O₃ can be present in an amount from about 4.0 to about 15 weight percent. The one or more RE₂O₃ can be present in an amount from about 5.0 to about 15 weight percent in some embodiments.

The amount of RE₂O₃ used in some embodiments can depend on the particular RE₂O₃ used, whether other types of RE₂O₃ are used in the composition, melt properties of the composition, and desired properties of the glass fibers to be formed from the composition, and others.

In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. In some embodiments, RE₂O₃ is selected from the group consisting of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. In some embodiments, RE₂O₃ is selected from the group consisting of La₂O₃ and Y₂O₃.

In some embodiments, RE₂O₃ used in glass compositions of the present invention can comprise La₂O₃ in an amount of about 0.05 weight percent or greater. In some embodiments, RE₂O₃ can comprise La₂O₃ in an amount of about 0.5 weight percent or greater. In some embodiments, RE₂O₃ can comprise La₂O₃ in an amount greater than about 2 weight percent. In some embodiments, RE₂O₃ can comprise La₂O₃ in an amount of about 3 weight percent or greater. In some embodiments, RE₂O₃ can comprise La₂O₃ in an amount from greater than about 2 weight percent to about 21 weight percent. In some embodiments, RE₂O₃ can comprise La₂O₃ in an amount from greater than about 2 weight percent to about 10 weight percent. In some embodiments, RE₂O₃ can comprise La₂O₃ in an amount from greater than about 2 weight percent to about 6 weight percent. In some embodiments, RE₂O₃ can comprise La₂O₃ in an amount from about 3 weight percent to about 10 weight percent. In some embodiments, RE₂O₃ can comprise La₂O₃ in an amount from about 3 weight percent to about 6 weight percent. In some embodiments, the glass composition can be substantially free of La₂O₃. As set forth above and in the Examples below, other amounts of La₂O₃ can also be included in glass compositions according to some embodiments. In some embodiments, the inclusion of La₂O₃ in glass compositions is believed to have a desirable impact on glass softening temperature and glass transition temperatures as well as on tensile strength, elongation, coefficient of thermal expansion, and other properties of glass fibers formed from the compositions.

In some embodiments, the RE₂O₃ used in glass compositions of the present invention can comprise Y₂O₃ in an amount of about 0.05 weight percent or greater. In some embodiments, RE₂O₃ can comprise Y₂O₃ in an amount of about 0.5 weight percent or greater. In some embodiments, Y₂O₃ can be present in an amount from about 0.05 to about 15 weight percent. In some embodiments, Y₂O₃ can be present in an amount up to about 6 weight percent. In some embodiments, Y₂O₃ can be present in an amount from about 3 to about 5.5 weight percent. In some embodiments, the Y₂O₃ content can be about 2 weight percent or less. In some embodiments, the glass composition can be substantially free of Y₂O₃. As set forth above and in the Examples below, other amounts of Y₂O₃ can also be included in glass compositions according to some embodiments. In some embodiments, the inclusion of Y₂O₃ in glass compositions is believed to have a desirable impact on glass softening temperature and glass transition temperature as well as on modulus, tensile strength, elongation, coefficient of thermal expansion, and other properties of glass fibers formed from the compositions.

In some embodiments, the RE₂O₃ used in glass compositions of the present invention can comprise Sc₂O₃ in an amount of about 0.05 weight percent or greater. In some embodiments, RE₂O₃ can comprise Sc₂O₃ in an amount of about 0.5 weight percent or greater. In some embodiments, Sc₂O₃ can be present in an amount from about 0.5 to about 4 weight percent. In some embodiments, the glass composition can be substantially free of Sc₂O₃. As set forth above and in the Examples below, other amounts of Sc₂O₃ can also be included in glass compositions according to some embodiments. In some embodiments, while the inclusion of Sc₂O₃ in glass compositions is believed to have a desirable impact on some properties of glass fibers formed from the compositions (e.g., glass softening temperature, glass transition temperature, coefficient of thermal expansion, etc.), the presence of Sc₂O₃ has also been observed to raise the liquidus temperature of the compositions.

In some embodiments, the RE₂O₃ used in glass compositions of the present invention can comprise Nd₂O₃ in an amount of about 0.05 weight percent or greater. In some embodiments, RE₂O₃ can comprise Sc₂O₃ in an amount of about 0.5 weight percent or greater. In some embodiments, Nd₂O₃ can be present in an amount from about 0.5 to about 15 weight percent. In some embodiments, the glass composition can be substantially free of Nd₂O₃. As set forth above and in the Examples below, other amounts of Nd₂O₃ can also be included in glass compositions according to some embodiments. In some embodiments, the inclusion of Nd₂O₃ in glass compositions is believed to have a desirable impact on glass softening temperature and glass transition temperature as well as on modulus, tensile strength, elongation, coefficient of thermal expansion, and other properties of glass fibers formed from the compositions.

Various combinations of RE₂O₃ can be also used to achieve desirable properties (e.g., tensile strength, modulus, specific strength, specific modulus, etc.). For example, the selection of a particular RE₂O₃ and its relative amount can impact the fiber density which can in turn impact specific strength (tensile strength divided by density) and specific modulus (modulus divided by density). Likewise, the selection of a particular RE₂O₃ and its relative amount can impact melt properties of the glass compositions. For example, as noted above, the presence of Sc₂O₃ in certain amounts can increase the liquidus temperature of a glass composition. Similarly, cerium oxide (Ce₂O₃ and CeO₂) can act as an oxidizing and fining agent, such that in some embodiments, the amount of cerium oxide can be no more than 2 weight percent. In some embodiments, the glass composition can be substantially free of cerium oxide. Finally, the selection of a particular RE₂O₃ and its relative amount can impact the cost of making the glass fibers due to its impact on melt properties and due its cost as a raw material as the cost of RE₂O₃ varies substantially.

As noted above, glass compositions of the present invention and in particular, fiberizable glass compositions also include other components including SiO₂, Al₂O₃, CaO, MgO, and others.

In one embodiment, a glass composition suitable for fiber forming comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). In some embodiments, MnO_(x) comprises MnO₂ in an amount of about 2 weight percent or greater. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises TiO₂ in an amount greater than about 3 weight percent. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

In another embodiment, a glass composition suitable for fiber forming comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments, BaO is present in an amount greater than about 2 weight percent. In some embodiments, SrO is present in an amount greater than about 2 weight percent. In some embodiments, ZnO is present in an amount greater than about 2 weight percent. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

In another embodiment, a glass composition suitable for fiber forming comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments, the composition comprises 0.5 weight percent or greater Cu₂O. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

In another embodiment, a glass composition suitable for fiber forming comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4. In some embodiments, La₂O₃ is present in an amount of about 3 weight percent or greater. In some embodiments, CaO is present in an amount less than about 1.5 weight percent and MgO is present in an amount greater than about 6 weight percent. In some embodiments, the SiO₂/Al₂O₃ ratio is greater than about 4.2. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

It should be understood that any component of a glass composition described as being present in amount from about 0 weight percent to another weight percent is not necessarily required in all embodiments. In other words, such components may be optional in some embodiments, depending of course on the amounts of other components included in the compositions. Likewise, in some embodiments, glass compositions can be substantially free of such components, meaning that any amount of the component present in the glass composition would result from the component being present as a trace impurity in a batch material. A component present as a trace impurity is not intentionally added to the glass composition. In other words, a trace impurity is present in a herein described glass composition by virtue of its presence as an impurity in a starting material added to the glass composition. Generally, a trace impurity is present in the glass composition in an amount no greater than about 0.1 weight percent, although some trace impurities may be present in the glass composition in an amount up to about 0.5 weight percent.

Some embodiments of the present invention can be characterized by the amount of SiO₂ present in the glass compositions. SiO₂ can be present in an amount from about 51 to about 70 weight percent in some embodiments. SiO₂ can be present in an amount from about 51 to about 66 weight percent in some embodiments. The SiO₂ content in some embodiments can be less than about 66 weight percent. SiO₂ can be present in an amount from about 51 to about 65 weight percent, and from about 51 to about 63 weight percent in some embodiments. SiO₂ can be present, in some embodiments, in an amount from about 54 to about 65 weight percent and from about 54 to about 63 weight percent. In some embodiments, SiO₂ can be present in an amount from about 58 to about 66 weight percent. In some embodiments, SiO₂ can be present in an amount from about 58 to about 64 weight percent. In some embodiments, SiO₂ can be present in an amount from about 59 to about 65 weight percent. In some embodiments, SiO₂ can be present in an amount from about 58 to about 70 weight percent. In some embodiments, SiO₂ can be present in an amount from about 65 to about 70 weight percent. The glass compositions, in some embodiments, can comprise at least about 60 weight percent SiO₂.

Some embodiments of the present invention can be characterized by the amount of Al₂O₃ present in the glass compositions. In some embodiments, glass compositions can comprise from about 12.5 to about 22 weight percent Al₂O₃. Al₂O₃ can be present, in some embodiments, in an amount from about 12.5 to about 19 weight percent. Al₂O₃ can be present in an amount from about 13 to about 22 weight percent in some embodiments. Al₂O₃ can be present in an amount from about 14.5 to about 19 weight percent in some embodiments. In some embodiments, Al₂O₃ can be present in an amount from about 15 to about 19 weight percent. In some embodiments, Al₂O₃ can be present in an amount from about 15 to about 18 weight percent.

Some embodiments of the present invention can be characterized by the ratio of SiO₂ content to Al₂O₃ content (SiO₂/Al₂O₃). The SiO₂/Al₂O₃ ratio can affect the Young's modulus of the glass compositions. In some embodiments, the SiO₂/Al₂O₃ ratio is about 2 or greater. In some embodiments, the SiO₂/Al₂O₃ ratio is about 3 or greater. In some embodiments, the SiO₂/Al₂O₃ ratio is about 3.5 or greater. In some embodiments, the SiO₂/Al₂O₃ ratio is about 3.8 or greater. In some embodiments, the SiO₂/Al₂O₃ ratio is about 4 or greater. In some embodiments, the SiO₂/Al₂O₃ ratio is about 4.2 or greater. In some embodiments, the SiO₂/Al₂O₃ ratio is about 4.5 or greater.

Some embodiments of the present invention can be characterized by the amount of CaO present in the glass compositions. CaO can be present in an amount from about 0 to about 20 weight percent in some embodiments. CaO can be present, in some embodiments, in an amount from about 0 and to 16 weight percent. In some embodiments, the CaO content can be less than 10 weight percent. In some embodiments, the CaO content can be less than 8 weight percent. In some embodiments, the CaO content can be less than 2 weight percent. In some embodiments, the CaO content can be 1.5 weight percent or less. In some embodiments, the CaO content can be 1 weight percent or less. In some embodiments, CaO can be present in an amount from about 10 to about 20 weight percent. In some embodiments, CaO can be present in an amount from about 12 to about 20 weight percent. In some embodiments, CaO can be present in an amount from about 15 to about 20 weight percent. In some embodiments, CaO can be present in an amount from about 0.5 to about 15 weight percent. Glass compositions of the present invention, in some embodiments, can comprise from about 0.5 to about 14 weight percent. In some embodiments, CaO can be present in an amount from about 0.5 to about 10 weight percent. In some embodiments, CaO can be present in an amount from about 2 to about 8 weight percent. In some embodiments, the glass composition can be substantially free of CaO.

Some embodiments of the present invention can be characterized by the amount of MgO present in the glass compositions. MgO can be present in an amount from about 0 to about 12.5 weight percent in some embodiments. In some embodiments, glass compositions of the present invention comprise from about 0 to about 12 weight percent MgO. MgO can be present in an amount from about 0 to about 11 weight percent in some embodiments. MgO can be present in an amount from greater than about 0 to about 11 weight percent in some embodiments. MgO can be present in an amount from about 1 to about 11 weight percent in some embodiments. MgO can be present in an amount from greater than about 0 to about 9 weight percent in some embodiments. MgO can be present in an amount of about 6 weight percent or greater in some embodiments. MgO can be present in an amount of about 6.5 weight percent or greater in some embodiments. MgO can be present, in some embodiments, in an amount from about 6.5 to about 12.5 weight percent. MgO can be present, in some embodiments, in an amount from about 7 to about 12.5 weight percent. MgO can be present, in some embodiments, in an amount from about 6 to about 9 weight percent. In some embodiments, the glass composition can be substantially free of MgO.

Some embodiments of the present invention can be characterized by the ratio of MgO content to CaO content (MgO/CaO). The MgO/CaO ratio may affect the Young's modulus and the liquidus temperature of the glass composition. In some embodiments in which MgO and CaO are present, the MgO/CaO ratio may be less than about 1. In some embodiments, the MgO/CaO ratio can be less than about 0.8. In some embodiments, the MgO/CaO ratio can be less than about 0.6. In some embodiments, the MgO/CaO ratio can be greater than about 4. In some embodiments, the MgO/CaO ratio can be greater than about 4.5 In some embodiments, the MgO/CaO ratio can be greater than about 5. In some embodiments, the MgO/CaO ratio can be greater than about 10.

Some embodiments of the present invention can be characterized by the amount of BaO present in the glass compositions. In some embodiments, BaO can be present in an amount greater than 0 weight percent, 0.5 weight percent or greater, 1 weight percent or greater, 2 weight percent or greater, or 3 weight percent or greater. BaO can be present in an amount from about 0 to about 4 weight percent in some embodiments. In some embodiments, glass compositions of the present invention comprise from about 0 to about 3.5 weight percent BaO. BaO can be present in an amount from greater than about 0 to about 4 weight percent in some embodiments. BaO can be present in an amount from about 0.5 to about 4 weight percent in some embodiments. BaO can be present in an amount from about 1 to about 4 weight percent in some embodiments. BaO can be present in an amount from about 2 to about 4 weight percent in some embodiments. BaO can be present in an amount from about 2.5 to about 4 weight percent in some embodiments. BaO can be present in an amount from about 3 to about 4 weight percent in some embodiments. In some embodiments, the glass composition can be substantially free of BaO.

Some embodiments of the present invention can be characterized by the amount of SrO present in the glass compositions. In some embodiments, SrO can be present in an amount greater than 0 weight percent, 0.5 weight percent or greater, 1 weight percent or greater, 2 weight percent or greater, or 3 weight percent or greater. SrO can be present in an amount from about 0 to about 4 weight percent in some embodiments. In some embodiments, glass compositions of the present invention comprise from about 0 to about 3.5 weight percent SrO. SrO can be present in an amount from greater than about 0 to about 4 weight percent in some embodiments. SrO can be present in an amount from about 0.5 to about 4 weight percent in some embodiments. SrO can be present in an amount from about 1 to about 4 weight percent in some embodiments. SrO can be present in an amount from about 2 to about 4 weight percent in some embodiments. SrO can be present in an amount from about 2.5 to about 4 weight percent in some embodiments. In some embodiments, the glass composition can be substantially free of SrO.

Some embodiments of the present invention can be characterized by the total amount of CaO, MgO, BaO, and SrO content (CaO+MgO+BaO+SrO). The CaO+MgO+BaO+SrO content can be 23 weight percent or less in some embodiments. The CaO+MgO+BaO+SrO content can be from about 1 to about 23 weight percent. The CaO+MgO+BaO+SrO content can be from about 8 to about 23 weight percent. The CaO+MgO+BaO+SrO content can be from about 9 to about 23 weight percent. The CaO+MgO+BaO+SrO content can be from about 9 to about 20 weight percent. The CaO+MgO+BaO+SrO content can be from about 9 to about 17 weight percent. The CaO+MgO+BaO+SrO content can be from about 0 to about 8 weight percent. The CaO+MgO+BaO+SrO content can be from about 1 to about 8 weight percent. The CaO+MgO+BaO+SrO content can be from about 1 to about 6 weight percent. The CaO+MgO+BaO+SrO content can be from about 1 to about 3 weight percent.

Some embodiments of the present invention can be characterized by the amount of ZnO present in the glass compositions. In some embodiments, ZrO can be present in an amount greater than 0 weight percent, 0.5 weight percent or greater, 1 weight percent or greater, 2 weight percent or greater, or 3 weight percent or greater. ZnO can be present in an amount from about 0 to about 5.5 weight percent in some embodiments. In some embodiments, glass compositions of the present invention comprise from about 0 to about 5 weight percent ZnO. ZnO can be present in an amount from greater than about 0 to about 5.5 weight percent in some embodiments. ZnO can be present in an amount from greater than about 0 to about 5 weight percent in some embodiments. ZnO can be present in an amount from about 1 to about 5 weight percent in some embodiments. ZnO can be present in an amount from about 1.5 to about 5 weight percent in some embodiments. ZnO can be present in an amount from about 2 to about 5 weight percent in some embodiments. ZnO can be present in an amount from about 2.5 to about 5 weight percent in some embodiments. ZnO can be present in an amount from about 4 to about 5 weight percent in some embodiments. In some embodiments, the glass composition can be substantially free of ZnO.

Some embodiments of the present invention can be characterized by the total amount of BaO, SrO, and ZnO content (BaO+SrO+ZnO). The BaO+SrO+ZnO content can be greater than 1 weight percent in some embodiments. The BaO+SrO+ZnO content can be 2 weight percent or greater in some embodiments. The BaO+SrO+ZnO content can be 2.5 weight percent or greater in some embodiments. The BaO+SrO+ZnO content can be 3 weight percent or greater in some embodiments. The BaO+SrO+ZnO content can be up to 10 weight percent in some embodiments. The BaO+SrO+ZnO content can be up to 6 weight percent in some embodiments. The BaO+SrO+ZnO content can be up to 5.5 weight percent in some embodiments. The BaO+SrO+ZnO content can be up to 5 weight percent in some embodiments. The BaO+SrO+ZnO content can be from 2 to 6 weight percent in some embodiments. The BaO+SrO+ZnO content can be from 2.5 to 5 weight percent in some embodiments. In some embodiments, the glass composition can be substantially free of any one of BaO, SrO, and ZnO. In some embodiments, the glass composition can be substantially free of any combination of BaO, SrO, and ZnO, including being substantially free of all of BaO, SrO, and ZnO.

Some embodiments of the present invention can be characterized by the amount of Na₂O present in the glass compositions. In some embodiments, glass compositions of the present invention can comprise from about 0 to about 2.5 weight percent Na₂O. Na₂O can be present, in some embodiments, in an amount from about 0 to about 1.5 weight percent. Na₂O can be present, in some embodiments, in an amount from about 0 to about 1 weight percent. In some embodiments, Na₂O can be present in an amount up to about 1.5 weight percent. Na₂O can be present, in some embodiments, in an amount up to about 1.0 weight percent. Na₂O can be present, in some embodiments, in an amount up to about 0.5 weight percent. Na₂O can be present, in some embodiments, in an amount up to about 0.25 weight percent. Na₂O can be present, in some embodiments, in an amount up to about 0.1 weight percent. In some embodiments, the glass composition can be substantially free of Na₂O.

Some embodiments of the present invention can be characterized by the amount of K₂O present in the glass compositions. K₂O can be present, in some embodiments, in an amount from about 0 to about 1 weight percent. In some embodiments, K₂O can be present in an amount up to about 1 weight percent. K₂O can be present, in some embodiments, in an amount up to about 0.5 weight percent. K₂O can be present, in some embodiments, in an amount up to about 0.3 weight percent. K₂O can be present, in some embodiments, in an amount up to about 0.1 weight percent. In some embodiments, the glass composition can be substantially free of K₂O.

Some embodiments of the present invention can be characterized by the amount of Li₂O present in the glass compositions. In some embodiments, glass compositions of the present invention can comprise from about 0 to about 2 weight percent Li₂O. Li₂O can be present, in some embodiments, in an amount from about 0 to about 1 weight percent. In some embodiments, Li₂O can be present from greater than about 0 to about 1 weight percent. Li₂O can be present, in some embodiments, in an amount from about 0.4 to about 2 weight percent. Li₂O can be present, in some embodiments, in an amount from about 0.4 to about 1 weight percent. Li₂O can be present, in some embodiments, in an amount from about 0.5 to about 1 weight percent. In some embodiments, the glass composition can be substantially free of Li₂O. Some embodiments of the present invention can be characterized by the total amount of Na₂O, K₂O, and Li₂O content (Na₂O+K₂O+Li₂O). In some embodiments, the Na₂O+K₂O+Li₂O content in glass compositions of the present invention is greater than about 1 weight percent. The Na₂O+K₂O+Li₂O content, in some embodiments, is up to about 2.5 weight percent. In some embodiments, the Na₂O+K₂O+Li₂O content is present in an amount greater than about 1 weight percent and up to about 2.5 weight percent. In some embodiments, the Na₂O+K₂O+Li₂O content in glass compositions of the present invention is from about 0 to about 1.5 weight percent. In some embodiments, the Na₂O+K₂O+Li₂O content in glass compositions of the present invention is from about 0 to about 1.0 weight percent. In some embodiments, the Na₂O+K₂O+Li₂O content in glass compositions of the present invention is from about 0 to about 0.8 weight percent. In some embodiments, the Na₂O+K₂O+Li₂O content in glass compositions of the present invention is from about 0 to about 0.6 weight percent.

Some embodiments of the present invention can be characterized by the amount of Cu₂O present in the glass compositions. Cu₂O can be present, in some embodiments, in an amount from about 0 to about 2.5 weight percent. Cu₂O can be present, in some embodiments, in an amount from about 0 to about 2 weight percent. Cu₂O can be present, in some embodiments, in an amount from about 0 to about 1.7 weight percent. Cu₂O can be present, in some embodiments, in an amount from greater than about 0 to about 2.5 weight percent. Cu₂O can be present, in some embodiments, in an amount from greater than about 0 to about 2 weight percent. Cu₂O can be present, in some embodiments, in an amount from greater than about 0 to about 1.7 weight percent. Cu₂O can be present, in some embodiments, in an amount of 0.5 weight percent or greater. Cu₂O can be present, in some embodiments, in an amount from about 0.5 to about 2.5 weight percent. Cu₂O can be present, in some embodiments, in an amount from about 0.5 to about 2 weight percent. Cu₂O can be present, in some embodiments, in an amount from about 0.5 to about 1.7 weight percent. In some embodiments, the glass composition can be substantially free of Cu₂O.

Some embodiments of the present invention can be characterized by the amount of B₂O₃ present in the glass compositions. B₂O₃ can be present in an amount from about 0 to about 3 weight percent in some embodiments. In some embodiments, B₂O₃ can be present in an amount from about 0 to about 2 weight percent or from about 0 to less than about 2 weight percent. B₂O₃ can be present, in some embodiments, in an amount from about 0 to about 1.5 weight percent. In some embodiments, the B₂O₃ content can be about 1 weight percent or less. In some embodiments, the B₂O₃ content can be about 0.5 weight percent or less. In some embodiments, glass compositions of the present invention can be substantially free of B₂O₃. In other embodiments, glass compositions of the present invention can comprise greater than about 1 weigh percent B₂O₃. In some embodiments, B₂O₃ can be present in an amount from greater than about 0 to about 10 weight percent.

Some embodiments of the present invention can be characterized by the amount of Fe₂O₃ present in the glass compositions. In some embodiments, Fe₂O₃ can be present in an amount from about 0 to about 1.0 weight percent. In some embodiments, Fe₂O₃ can be about 0.5 weight percent or less. In some embodiments, Fe₂O₃ can be present in an amount from greater than about 0 to about 1.0 weight percent. Fe₂O₃ can be present, in some embodiments, in an amount from greater than about 0 to about 0.5 weight percent. In some embodiments, Fe₂O₃ can be present in an amount from greater than about 0 to about 0.4 weight percent. Fe₂O₃ can be present, in some embodiments, from about 0.1 to about 1.0 weight percent. Fe₂O₃ can be present, in some embodiments, from about 0.2 to about 1.0 weight percent. Fe₂O₃ can be present, in some embodiments, from about 0.25 to about 1.0 weight percent. Fe₂O₃ can be present, in some embodiments, from about 0.3 to about 1.0 weight percent. Fe₂O₃ can be present, in some embodiments, from about 0.2 to about 0.8 weight percent, or from about 0.2 to about 0.5 weight percent. Fe₂O₃ can be present, in some embodiments, from about 0.25 to about 0.8 weight percent, or from about 0.25 to about 0.5 weight percent. Fe₂O₃ can be present, in some embodiments, from about 0.3 to about 0.8 weight percent, or from about 0.3 to about 0.5 weight percent.

Some embodiments of the present invention can be characterized by the amount of TiO₂ present in the glass compositions. TiO₂ can be present, in some embodiments, in an amount greater than 0 weight percent, 1.5 weight percent or greater, 3 weight percent or greater, 4 weight percent or greater, or 5 weight percent or greater. TiO₂ can be present, in some embodiments, in an amount from about 0 to about 9 weight percent. TiO₂ can be present, in some embodiments, in an amount from greater than about 1.5 to about 9 weight percent. TiO₂ can be present, in some embodiments, in an amount from greater than about 3 to about 9 weight percent. TiO₂ can be present, in some embodiments, in an amount from greater than about 4 to about 9 weight percent. TiO₂ can be present, in some embodiments, in an amount from about 5 to about 9 weight percent. TiO₂ can be present, in some embodiments, in an amount from about 0 to about 3 weight percent. TiO₂ can be present, in some embodiments, in an amount from about 0 to about 2 weight percent. TiO₂ can be present, in some embodiments, in an amount from about 0 to about 1 weight percent. In some embodiments, TiO₂ can be present in an amount from greater than 0 to about 3 weight percent. In some embodiments, the glass composition can be substantially free of TiO₂.

Some embodiments of the present invention can be characterized by the amount of ZrO₂ present in the glass compositions. ZrO₂ can be present, in some embodiments, in an amount from about 0 to about 3 weight percent. In some embodiments, ZrO₂ can be present in an amount up to about 2 weight percent. In some embodiments, glass compositions of the present invention can be substantially free of ZrO₂.

Some embodiments of the present invention can be characterized by the amount of MnO present in the glass compositions. As used herein, the term MnO_(x) refers to the genus consisting of MnO and MnO₂. As used throughout, a range of MnO_(x) can include any amount of MnO and MnO₂ which, in sum, are within the range of MnO_(x). By way of example, a range from about 0 to about 9.5 MnO_(x) can include (i) about 0 weight percent MnO and about 9.5 weight percent MnO₂, (ii) about 9.5 weight percent MnO and about 0 weight percent MnO₂, or (iii) any weight percent combination of MnO and MnO_(x) within the range from about 0 to about 9.5 weight percent. MnO_(x) can be present, in some embodiments, in an amount of about 1 weight percent or greater, about 1.5 weight percent or greater, about 2 weight percent or greater, about 3 weight percent or greater, or about 4 weight percent or greater. MnO_(x) can be present, in some embodiments, in an amount from about 0 to about 9.5 weight percent. MnO_(x) can be present, in some embodiments, in an amount from greater than about 0 to about 9.5 weight percent. MnO_(x) can be present, in some embodiments, in an amount from about 1 to about 9.5 weight percent. MnO_(x) can be present, in some embodiments, in an amount from about 1.5 to about 9.5 weight percent. MnO can be present, in some embodiments, in an amount from about 2 to about 9.5 weight percent. MnO_(x) can be present, in some embodiments, in an amount from about 4 to about 9.5 weight percent. In some embodiments in which MnO is present, MnO can be present in an amount greater than about 2 weight percent. Thus, the MnO_(x) content can be greater than about 1 weight percent, wherein if MnO is present, then MnO is present an amount of about 2 weight percent or greater. In some embodiments, MnO_(x) consists essentially of MnO in an amount from about 0 to about 8.5 weight percent. In some embodiments, MnO_(x) consists essentially of MnO in an amount from about 1.5 to about 8.5 weight percent. In some embodiments, MnO_(x) consists essentially of MnO in an amount from about 2 to about 8 weight percent. In some embodiments, MnO_(x) consists essentially of MnO₂ in an amount from about 0 to about 9.5 weight percent. In some embodiments, MnO_(x) consists essentially of MnO₂ in an amount from about 1.5 to about 9.5 weight percent. In some embodiments, MnO_(x) consists essentially of MnO₂ in an amount from about 4 to about 9.5 weight percent. In some embodiments, glass compositions of the present invention can be substantially free of MnO, MnO₂, or MnO_(x).

Some embodiments of the present invention can be characterized by the amount of P₂O₅ present in the glass compositions. P₂O₅ can be present, in some embodiments, in an amount from about 0 to about 3 weight percent. In some embodiments, P₂O₅ can be present in an amount up to about 2.5 weight percent. In some embodiments, glass compositions of the present invention can be substantially free of P₂O₅.

Sulfate (expressed as SO₃) may also be present as a refining agent. Small amounts of impurities may also be present from raw materials or from contamination during the melting processes, such as Cl₂, Cr₂O₃, or NiO (not limited to these particular chemical forms). Other refining agents and/or processing aids may also be present such as As₂O₃, Sb₂O₃, SnO₂ or CeO₂ (not limited to these particular chemical forms). These impurities and refining agents, when present, are each typically present in amounts less than about 0.5% by weight of the total glass composition. In some embodiments, the glass composition can be substantially free of any one of these refining agents, or can be substantially free of any combination of these refining agents. Some embodiments of the present invention can be characterized by the presence of an additional feature in the glass compositions. The additional feature is not particularly limited. The additional feature can comprise any one or more compound(s), component(s), and/or ratio(s) in any amount(s) or range(s) disclosed herein. In some embodiments, the additional feature can comprise La₂O₃ in an amount greater than about 2 weight percent. In some embodiments, the additional feature can comprise CaO in an amount less than about 2 weight percent. In some embodiments, the additional feature can comprise a MgO/CaO ratio less than about 1. In some embodiments, the additional feature can comprise a SiO₂/Al₂O₃ ratio greater than about 4.

As noted above, glass compositions, according to some embodiments of the present invention are fiberizable. In some embodiments, glass compositions of the present invention have forming temperatures (T_(F)) desirable for use in commercial fiber glass manufacturing operations. As used herein, the term “forming temperature” or T_(F), means the temperature at which the glass composition has a viscosity of 1000 poise (or “log 3 temperature”). Glass compositions of the present invention, in some embodiments, have a forming temperature (T_(F)) ranging from about 1250° C. to about 1550° C. In another embodiment, glass compositions of the present invention have a forming temperature ranging from about 1250° C. to about 1415° C. In another embodiment, glass compositions of the present invention have a forming temperature ranging from about 1250° C. to about 1350° C. In some embodiments, glass compositions have a forming temperature ranging from about 1250° C. to about 1310° C.

Glass compositions of the present invention, in some embodiments, have a liquidus temperature ranging from about 1150° C. to about 1515° C. In another embodiment, glass compositions of the present invention have a liquidus temperature ranging from about 1190° C. to about 1515° C. In another embodiment, glass compositions of the present invention have a liquidus temperature ranging from about 1190° C. to about 1300° C. In some embodiments, glass compositions of the present invention have a liquidus temperature ranging from about 1190° C. to about 1260° C.

In some embodiments, the difference between the forming temperature and the liquidus temperature of a glass composition of the present invention is desirable for commercial fiber glass manufacturing operations. For example, for some embodiments of glass compositions, the difference between the forming temperature and the liquidus temperature ranges from about 25° C. to greater than 60° C. In some embodiments, the difference between the forming temperature and the liquidus temperature of a glass composition of the present invention ranges from about 35° C. to greater than 60° C. In some embodiments, the difference between the forming temperature and the liquidus temperature of a glass composition of the present invention is at least 50° C. In some embodiments, the difference between the forming temperature and the liquidus temperature of a glass composition of the present invention is up to 200° C.

As provided herein, glass fibers can be formed from some embodiments of the glass compositions of the present invention. Thus, embodiments of the present invention can comprise glass fibers formed from any of the glass compositions described herein. In some embodiments, the glass fibers may be arranged into a fabric. In some embodiments, glass fibers of the present invention can be provided in other forms including, for example and without limitation, as continuous strands, chopped strands (dry or wet), yarns, rovings, prepregs, etc. In short, various embodiments of the glass compositions (and any fibers formed therefrom) can be used in a variety of applications.

Some embodiments of the present invention relate to fiber glass strands. Some embodiments of the present invention relate to yarns comprising fiber glass strands. Some embodiments of yarns of the present invention are particularly suitable for weaving applications. In addition, some embodiments of the present invention relate to glass fiber fabrics. Some embodiments of fiber glass fabrics of the present invention are particularly suitable for use in reinforcement applications, especially reinforcement applications in which high modulus, high strength, and/or high elongation are important. Further, some embodiments of the present invention relate to composites that incorporate fiber glass strands, fiber glass yarns, and fiber glass fabrics, such as fiber reinforced polymer composites. Some composites of the present invention are particularly suitable for use in reinforcement applications, especially reinforcement applications in which high modulus, high strength, and/or high elongation are important, such as wind energy (e.g., windmill blades), automotive applications, safety/security applications (e.g., ballistics armor or armor panels), aerospace or aviation applications (e.g., interior floors of planes), high pressure vessels or tanks, missile casings, and others. Some embodiments of the present invention relate to automotive composites. Some embodiments of the present invention relate to aerospace composites. Other embodiments of the present application relate to aviation composites. Still other embodiments of the present invention relate to composites suitable for use in wind energy applications. Some embodiments of the present invention relate to prepregs. Some embodiments of the present invention relate to composites for safety/security applications such as armor panels. Other embodiments of the present invention relate to composites for high pressure vessels or storage tanks. Some embodiments of the present invention relate to composites for missile casings. Other embodiments of the present invention relate to composites for use in high temperature thermal insulation applications. Some embodiments of the present invention relate to printed circuit boards where lower coefficients of thermal expansion are particularly desirable such as substrates for chip packaging.

Some embodiments of the present invention relate to fiber glass strands. In some embodiments, a fiber glass strand of the present invention comprises a plurality of glass fibers comprising a glass composition that comprises the following components:

SiO₂ from about 51 to about 70 weight percent; Al₂O₃ from about 12.5 to about 22 weight percent; CaO from about 0 to about 20 weight percent; MgO from about 0 to about 11 weight percent; Fe₂O₃ from about 0.2 to about 1 weight percent; RE₂O₃ about 0.05 or greater weight percent; and MnO_(x) greater than about 1 weight percent.

In some embodiments, MnO_(x) comprises MnO₂ in an amount of about 2 weight percent or greater. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises TiO₂ in an amount greater than about 3 weight percent. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

In some embodiments, a fiber glass strand of the present invention comprises a plurality of glass fibers comprising a glass composition that comprises the following components:

SiO₂ from about 51 to about 70 weight percent; Al₂O₃ from about 12.5 to about 22 weight percent; CaO from about 0 to about 20 weight percent; MgO from about 0 to about 11 weight percent; Fe₂O₃ from about 0.2 to about 1 weight percent; RE₂O₃ about 0.05 or greater weight percent; BaO from about 0 to about 4 weight percent; SrO from about 0 to about 4 weight percent; and ZnO from about 0 to about 5.5 weight percent;

wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent.

In some embodiments, BaO is present in an amount greater than about 2 weight percent. In some embodiments, SrO is present in an amount greater than about 2 weight percent. In some embodiments, ZnO is present in an amount greater than about 2 weight percent. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

In some embodiments, a fiber glass strand of the present invention comprises a plurality of glass fibers comprising a glass composition that comprises the following components:

SiO₂ from about 51 to about 70 weight percent; Al₂O₃ from about 12.5 to about 22 weight percent; CaO from about 0 to about 20 weight percent; MgO from about 0 to about 11 weight percent; Fe₂O₃ from about 0.2 to about 1 weight percent; RE₂O₃ about 0.05 or greater weight percent; and Cu₂O from greater than about 0 to about 2.5 weight percent.

In some embodiments, the composition comprises 0.5 weight percent or greater Cu₂O. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

In some embodiments, a fiber glass strand of the present invention comprises a plurality of glass fibers comprising a glass composition that comprises the following components:

SiO₂ from about 51 to about 70 weight percent; Al₂O₃ from about 12.5 to about 22 weight percent; CaO from about 0 to about 20 weight percent; MgO from about 0 to about 12.5 weight percent; Fe₂O₃ from about 0.2 to about 1 weight percent; RE₂O₃ about 0.05 or greater weight percent; and at least one additional feature selected from the group consisting of: La₂O₃ is present in an amount greater than about 2 weight percent; CaO is present in an amount less than about 2 weight percent; a MgO/CaO ratio less than about 1; and a SiO₂/Al₂O₃ ratio greater than about 4.

In some embodiments, the additional feature comprises La₂O₃ in an amount of about 3 weight percent or greater. In some embodiments, MgO is present in an amount greater than about 6 weight percent, and the additional feature comprises CaO in an amount less than about 1.5 weight percent. In some embodiments, the additional feature comprises the SiO₂/Al₂O₃ ratio in an amount greater than about 4.2. In some embodiments, RE₂O₃ comprises at least one of La₂O₃, Y₂O₃, Sc₂O₃, and Nd₂O₃. RE₂O₃ is present in an amount of at least about 1 weight percent in some embodiments. In some embodiments, the composition further comprises less than about 1.5 weight percent Na₂O+K₂O+Li₂O.

A number of other glass compositions are disclosed herein as part of the present invention, and other embodiments of the present invention relate to fiber glass strands formed from such compositions.

In some embodiments, glass fibers of the present invention can exhibit desirable mechanical and other properties. Glass fibers of the present invention, in some embodiments, can exhibit one or more improved mechanical properties relative to glass fibers formed from E-glass. In some embodiments, glass fibers of the present invention can provide one or more improved properties relative to glass fibers formed from R-glass and/or S-glass. Examples of desirable properties exhibited by some embodiments of glass fibers of the present invention include, without limitation, tensile strength, Young's modulus, coefficient of thermal expansion, softening point, elongation, and dielectric constant.

Glass fibers of the present invention can have desirable Young's modulus (E) values in some embodiments. In some embodiments, fibers formed from glass compositions of the present invention can have a Young's modulus greater than about 87 GPa. In some embodiments, glass fibers of the present invention can have a Young's modulus greater than about 90 GPa. Fibers formed from glass compositions of the present invention can have a Young's modulus greater than about 92 GPa in some embodiments. In some embodiments, glass fibers of the present invention can have a Young's modulus greater than about 93 GPa. Glass fibers of the present invention can have a Young's modulus greater than about 95 GPa in some embodiments. Unless otherwise stated herein, Young's modulus values discussed herein are determined using the procedure set forth in the Examples section below.

Glass fibers of the present invention, in some embodiments, can have desirable tensile strengths. In some embodiments, glass fibers of the present invention can have a tensile strength greater than 4000 MPa. Glass fibers of the present invention, in some embodiments, can have a tensile strength greater than 4,500 MPa. In some embodiments, glass fibers of the present invention can have a tensile strength greater than about 5000 MPa. Glass fibers of the present invention, in some embodiments, can have a tensile strength greater than about 5500 MPa. Unless otherwise stated herein, tensile strength values are determined using the procedure set forth in the Examples section.

Glass fibers of the present invention, in some embodiments, can have desirable elongation values. In some embodiments, glass fibers of the present invention can have an elongation of at least 5.0%. Glass fibers of the present invention can have an elongation of at least 5.5% in some embodiments. Unless otherwise stated herein, elongation values are determined using the procedure set forth in the Examples section.

Glass fibers of the present invention, in some embodiments, can have desirable coefficients of thermal expansion. In some embodiments, glass fibers of the present invention can have a coefficient of thermal expansion less than about 4.5 ppm/° C. Glass fibers of the present invention, in some embodiments, can have a coefficient of thermal expansion less than about 3.1 ppm/° C. Unless otherwise stated, coefficients of thermal expansion are determined using the procedure set forth in the Examples section.

Glass fibers of the present invention, in some embodiments, can have desirable softening points. In some embodiments, glass fibers of the present invention can have a softening point of at least about 900° C. Glass fibers of the present invention, in some embodiments, can have a softening point of at least about 950° C. Unless otherwise stated, softening point values are determined using the procedure set forth in the Examples section.

Glass fibers of the present invention, in some embodiments, can have dielectric constant values (D_(k)) desirable for use in electronics applications. In some embodiments, glass fibers of the present invention can have a dielectric constant value (D_(k)) of less than about 6.0 at 1 MHz frequency. Unless otherwise stated herein, dielectric constant (D_(k)) is determined from 1 MHz to 1 GHz by ASTM Test Method D150—“Standard Test Methods for A-C Loss Characteristics and Permittivity (Dielectric Constant) of Solid Electrical Insulating Materials.”

Fiber glass strands can comprise glass fibers of various diameters, depending on the desired application. In some embodiments, a fiber glass strand of the present invention comprises at least one glass fiber having a diameter between about 5 and about 18 μm. In other embodiments, the at least one glass fiber has a diameter between about 5 and about 10 μm.

In some embodiments, fiber glass strands of the present invention can be formed into rovings. Rovings can comprise assembled, multi-end, or single-end direct draw rovings. Rovings comprising fiber glass strands of the present invention can comprise direct draw single-end rovings having various diameters and densities, depending on the desired application. In some embodiments, a roving comprising fiber glass strands of the present invention exhibits a density up to about 112 yards/pound.

Some embodiments of the present invention relate to yarns comprising at least one fiber glass strand as disclosed herein. In some embodiments, a yarn of the present invention comprises at least one fiber glass strand comprising a glass composition that comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). A yarn, in some embodiments, comprises at least one fiber glass strand comprising a glass composition that comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments, a yarn of the present invention comprises at least one fiber glass strand comprising a glass composition that comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments, a yarn of the present invention comprises at least one fiber glass strand comprising a glass composition that comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4. In other embodiments, a yarn of the present invention can comprise at least one fiber glass strand comprising one of the other glass compositions disclosed herein as part of the present invention.

In some embodiments, a yarn of the present invention comprises at least one fiber glass strand as disclosed herein, wherein the at least one fiber glass strand is at least partially coated with a sizing composition. In some embodiments, the sizing composition is compatible with a thermosetting polymeric resin. In other embodiments, the sizing composition can comprise a starch-oil sizing composition.

Yarns can have various linear mass densities, depending on the desired application. In some embodiments, a yarn of the present invention has a linear mass density from about 5,000 yards/pound to about 10,000 yards/pound.

Yarns can have various twist levels and directions, depending on the desired application. In some embodiments, a yarn of the present invention has a twist in the z direction of about 0.5 to about 2 turns per inch. In other embodiments, a yarn of the present invention has a twist in the z direction of about 0.7 turns per inch.

Yarns can be made from one or more strands that are twisted together and/or plied, depending on the desired application. Yarns can be made from one or more strands that are twisted together but not plied; such yarns are known as “singles.” Yarns of the present invention can be made from one or more strands that are twisted together but not plied. In some embodiments, yarns of the present invention comprise 1-4 strands twisted together. In other embodiments, yarns of the present invention comprise 1 twisted strand.

Some embodiments of the present invention relate to fabrics comprising at least one fiber glass strand as disclosed herein. In some embodiments, a fabric of the present invention comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). A fabric, in some embodiments, comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments, a fabric of the present invention comprises at least one fiber glass strand comprising a glass composition that comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments, a fabric of the present invention comprises at least one fiber glass strand comprising a glass composition that comprises from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4. In other embodiments, a fabric of the present invention can comprise at least one fiber glass strand comprising one of the other glass compositions disclosed herein as part of the present invention.

In some embodiments of the present invention comprising a fabric, the glass fiber fabric is a fabric woven in accordance with industrial fabric style no. 7781. In other embodiments, the fabric comprises a plain weave fabric, a twill fabric, a crowfoot fabric, a satin weave fabric, a stitch bonded fabric (also known as a non-crimp fabric), or a “three-dimensional” woven fabric. Some embodiments of the present invention relate to composites. In some embodiments, a composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). A composite of the present invention, in some embodiments, comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments, a composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments, a composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4.

In other embodiments, a composite of the present invention can comprise a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers was formed from one of the other glass compositions disclosed herein as part of the present invention. In some embodiments, a composite of the present invention comprises a polymeric resin and at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In some embodiments, a composite of the present invention comprises a polymeric resin and at least a portion of a roving comprising at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In other embodiments, a composite of the present invention comprises a polymeric resin and at least one yarn as disclosed herein disposed in the polymeric resin. In still other embodiments, a composite of the present invention comprises a polymeric resin and at least one fabric as disclosed herein disposed in the polymeric resin. In some embodiments, a composite of the present invention comprises at least one fill yarn comprising at least one fiber glass strand as disclosed herein and at least one warp yarn comprising at least one fiber glass strand as disclosed herein.

Composites of the present invention can comprise various polymeric resins, depending on the desired properties and applications. In some embodiments of the present invention comprising a composite, the polymeric resin comprises an epoxy resin. In other embodiments of the present invention comprising a composite, the polymeric resin can comprise polyethylene, polypropylene, polyamide, polyimide, polybutylene terephthalate, polycarbonate, thermoplastic polyurethane, phenolic, polyester, vinyl ester, polydicyclopentadiene, polyphenylene sulfide, polyether ether ketone, cyanate esters, bis-maleimides, and thermoset polyurethane resins.

Some embodiments of the present invention relate to aerospace composites. In some embodiments, an aerospace composite of the present invention exhibits properties desirable for use in aerospace applications, such as high strength, high elongation, high modulus, and/or low density.

In some embodiments, an aerospace composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). An aerospace composite of the present invention, in some embodiments, comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments, an aerospace composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments, an aerospace composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4. In other embodiments, an aerospace composite of the present invention can comprise a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers was formed from one of the other glass compositions disclosed herein as part of the present invention.

In some embodiments, an aerospace composite of the present invention comprises a polymeric resin and at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In some embodiments, an aerospace composite of the present invention comprises a polymeric resin and at least a portion of a roving comprising at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In other embodiments, an aerospace composite of the present invention comprises a polymeric resin and at least one yarn as disclosed herein disposed in the polymeric resin. In still other embodiments, an aerospace composite of the present invention comprises a polymeric resin and at least one fabric as disclosed herein disposed in the polymeric resin. In some embodiments, an aerospace composite of the present invention comprises at least one fill yarn comprising at least one fiber glass strand as disclosed herein and at least one warp yarn comprising at least one fiber glass strand as disclosed herein.

Aerospace composites of the present invention can comprise various polymeric resins, depending on the desired properties and applications. In some embodiments of the present invention comprising an aerospace composite, the polymeric resin comprises an epoxy resin. In other embodiments of the present invention comprising an aerospace composite, the polymeric resin can comprise polyethylene, polypropylene, polyamide, polyimide, polybutylene terephthalate, polycarbonate, thermoplastic polyurethane, phenolic, polyester, vinyl ester, polydicyclopentadiene, polyphenylene sulfide, polyether ether ketone, cyanate esters, bis-maleimides, and thermoset polyurethane resins. Examples of parts in which aerospace composites of the present invention might be used can include, but are not limited to floor panels, overhead bins, galleys, seat back, and other internal compartments that are potentially prone to impact, as well as external components such as helicopter rotor blades.

Some embodiments of the present invention relate to aviation composites. In some embodiments, an aviation composite of the present invention exhibits properties desirable for use in aviation applications, such as high strength, high elongation, high modulus, lower density, high specific strength, and/or high specific modulus. The high elongation of some aviation composites of the present invention can make such composites especially desirable for use in aviation applications in which high impact resistance is important, such as aircraft interior applications. In some embodiments, aviation composites of the present invention can demonstrate increased impact performance as compared to composites formed from E-glass fabrics. Aviation composites of the present invention can be suitable for use in aircraft interiors (including, among other things, luggage storage bins, seats, and floors).

In some embodiments, an aviation composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). An aviation composite of the present invention, in some embodiments, comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments, an aviation composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments, an aviation composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4. In other embodiments, an aviation composite of the present invention can comprise a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers was formed from one of the other glass compositions disclosed herein as part of the present invention.

In some embodiments, an aviation composite of the present invention comprises a polymeric resin and at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In some embodiments, an aviation composite of the present invention comprises a polymeric resin and at least a portion of a roving comprising at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In other embodiments, an aviation composite of the present invention comprises a polymeric resin and at least one yarn as disclosed herein disposed in the polymeric resin. In still other embodiments, an aviation composite of the present invention comprises a polymeric resin and at least one fabric as disclosed herein disposed in the polymeric resin. In some embodiments, an aviation composite of the present invention comprises at least one fill yarn comprising at least one fiber glass strand as disclosed herein and at least one warp yarn comprising at least one fiber glass strand as disclosed herein.

Aviation composites of the present invention can comprise various polymeric resins, depending on the desired properties and applications. In some embodiments of the present invention comprising an aviation composite, the polymeric resin comprises a phenolic resin. In other embodiments of the present invention comprising an aviation composite, the polymeric resin can comprise epoxy, polyethylene, polypropylene, polyamide, polyimide, polybutylene terephthalate, polycarbonate, thermoplastic polyurethane, phenolic, polyester, vinyl ester, polydicyclopentadiene, polyphenylene sulfide, polyether ether ketone, cyanate esters, bis-maleimides, and thermoset polyurethane resins. Examples of parts in which aviation composites of the present invention might be used can include, but are not limited to, floor panels, overhead bins, galleys, seat back, and other internal compartments that are potentially prone to impact, as well as external components such as helicopter rotor blades.

Some embodiments of the present invention relate to automotive composites. In some embodiments, an automotive composite of the present invention exhibits properties desirable for use in automotive applications, such as high strength, high elongation and low fiber density. The combination of high strength and high elongation (or failure-to-strain) of some composites of the present invention can make such composites especially desirable for use in automotive applications in which high impact resistance is important, such as automobile structural components, bodies, and bumpers. In some embodiments, automotive composites of the present invention can demonstrate increased impact performance as compared to composites formed from E-glass fabrics, R-glass fabrics, and/or S-glass fabrics.

In some embodiments, an automotive composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). An automotive composite of the present invention, in some embodiments, comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments, an automotive composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments, an automotive composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4. In other embodiments, an automotive composite of the present invention can comprise a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers was formed from one of the other glass compositions disclosed herein as part of the present invention.

In some embodiments, an automotive composite of the present invention comprises a polymeric resin and at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In some embodiments, an automotive composite of the present invention comprises a polymeric resin and at least a portion of a roving comprising at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In other embodiments, an automotive composite of the present invention comprises a polymeric resin and at least one yarn as disclosed herein disposed in the polymeric resin. In still other embodiments, an automotive composite of the present invention comprises a polymeric resin and at least one fabric as disclosed herein disposed in the polymeric resin. In some embodiments, an automotive composite of the present invention comprises at least one fill yarn comprising at least one fiber glass strand as disclosed herein and at least one warp yarn comprising at least one fiber glass strand as disclosed herein.

Automotive composites of the present invention can comprise various polymeric resins, depending on the desired properties and applications. In some embodiments of the present invention comprising an automotive composite, the polymeric resin can comprise a thermoplastic resin or a thermosetting resin. Examples of common thermoplastic resins used in automotive composites include, without limitation, polypropylene, polyamide, high temperature polyamide, polyester, and other thermoplastic resins known to those of skill in the art. Examples of common thermosetting resins used in automotive composites include, without limitation, epoxy, phenolic, polyester, and other thermosetting resins known to those of skill in the art. Examples of parts in which automotive composites of the present invention might be used can include, but are not limited to, automobile structural components, bodies, and bumpers.

Some embodiments of the present invention relate to composites that can be used in wind energy applications. In some embodiments, a composite of the present invention suitable for use in wind energy applications exhibits properties desirable for use in wind energy applications, such as high modulus, high elongation, low fiber density, and/or high specific modulus. Composites of the present invention can be suitable for use in wind turbine blades, particularly long wind turbine blades that are lighter weight but still strong compared to other long wind turbine blades.

In some embodiments, a composite of the present invention suitable for use in wind energy applications comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). A composite of the present invention suitable for use in wind energy applications, in some embodiments, comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments, a composite of the present invention suitable for use in wind energy applications comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments, a composite of the present invention suitable for use in wind energy applications comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4. In other embodiments, a composite suitable for use in wind energy applications of the present invention can comprise a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers was formed from one of the other glass compositions disclosed herein as part of the present invention.

In some embodiments, a composite of the present invention suitable for use in wind energy applications comprises a polymeric resin and at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In some embodiments, a composite of the present invention suitable for use in wind energy applications comprises a polymeric resin and at least a portion of a roving comprising at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In other embodiments, a composite of the present invention suitable for use in wind energy applications comprises a polymeric resin and at least one yarn as disclosed herein disposed in the polymeric resin. In still other embodiments, a composite of the present invention suitable for use in wind energy applications comprises a polymeric resin and at least one fabric as disclosed herein disposed in the polymeric resin. In some embodiments, a composite of the present invention suitable for use in wind energy applications comprises at least one fill yarn comprising at least one fiber glass strand as disclosed herein and at least one warp yarn comprising at least one fiber glass strand as disclosed herein.

Composites of the present invention suitable for use in wind energy applications can comprise various polymeric resins, depending on the desired properties and applications. In some embodiments of the present invention comprising a composite suitable for use in wind energy applications, the polymeric resin comprises an epoxy resin. In other embodiments of the present invention comprising a composite suitable for use in wind energy applications, the polymeric resin can comprise polyester resins, vinyl esters, thermoset polyurethanes, or polydicyclopentadiene resins.

Some embodiments of the present invention relate to composites for use in high pressure vessels and/or tanks. In some embodiments, a composite for use in high pressure vessels and/or tanks of the present invention exhibits properties desirable for use in such applications, such as high strength, high elongation, low density, and/or high specific strength.

In some embodiments, a composite for use in high pressure vessels and/or tanks of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). A composite for use in high pressure vessels and/or tanks of the present invention, in some embodiments, comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments, a composite for use in high pressure vessels and/or tanks of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments, a composite for use in high pressure vessels and/or tanks of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4. In other embodiments, a composite for use in high pressure vessels and/or tanks of the present invention can comprise a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers was formed from one of the other glass compositions disclosed herein as part of the present invention.

In some embodiments, a composite for use in high pressure vessels and/or tanks of the present invention comprises a polymeric resin and at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In some embodiments, a composite for use in high pressure vessels and/or tanks of the present invention comprises a polymeric resin and at least a portion of a roving comprising at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In other embodiments, a composite for use in high pressure vessels and/or tanks of the present invention comprises a polymeric resin and at least one yarn as disclosed herein disposed in the polymeric resin. In still other embodiments, a composite for use in high pressure vessels and/or tanks of the present invention comprises a polymeric resin and at least one fabric as disclosed herein disposed in the polymeric resin. In some embodiments, a composite for use in high pressure vessels and/or tanks of the present invention comprises at least one fill yarn comprising at least one fiber glass strand as disclosed herein and at least one warp yarn comprising at least one fiber glass strand as disclosed herein.

Composites for use in high pressure vessels and/or tanks of the present invention can comprise various polymeric resins, depending on the desired properties and applications. In some embodiments of the present invention comprising a composite for use in high pressure vessels and/or tanks, the polymeric resin can comprise a thermosetting resin. Examples of common thermosetting resins used in high pressure vessels and/or tanks include, without limitation, epoxy, phenolic, polyester, vinyl ester and other thermosetting resins known to those of skill in the art.

In some embodiments, composites of the present invention can be useful in safety and/or security applications. For example, composites of the present invention, in some embodiments, are suitable for use in high mechanical stress applications, including, but not limited to, high energy impact applications. Glass fibers useful in some embodiments of the present invention can exhibit properties especially desirable for high energy impact applications such as ballistic or blast resistance applications. Compared to glass fibers comprising E-glass, glass fibers useful in some embodiments of the present invention can exhibit low dielectric constant, low dielectric loss, high glass transition temperature and/or low thermal expansion.

In some embodiments, composites of the present invention can be suitable for use in armor applications. For example, some embodiments of composites can be used in the production of armor panels. In some embodiments, a composite of the present invention can be formed into a panel, wherein the panel are expected to exhibit desirable 0.30 cal FSP (“fragment simulating projectile”) V50 values (e.g., at least about 900 feet per second (fps) at a panel areal density of about 2 lb/ft² and a panel thickness of about 5-6 mm) when measured by the U.S. Department of Defense Test Method Standard for V50 Ballistic Test for Armor, MIL-STD-662F, December 1997 (hereinafter “MIL-STD-662F”), the entirety of which is incorporated herein by reference. In this context, the term “composite” refers generically to a material comprising a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, whereas the term “panel” refers to a composite having sheet-like physical dimensions or shape. In other embodiments, a composite of the present invention can be formed into a panel, wherein the panel is expected to exhibit desirable 0.50 cal FSP V50 values (e.g., at least about 1200 fps at a panel areal density of about 4.8-4.9 lb/ft² and a panel thickness of about 13-13.5 mm) when measured by MIL-STD-662F. As V50 values can depend on the panel areal density and the panel thickness, composites of the present invention can have different V50 values depending on how the panel is constructed. One advantage of some embodiments of the present invention is the provision of composites having higher V50 values than similarly constructed composites assembled using E-glass fibers.

In some embodiments, a composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x), wherein the composite is adapted for use in ballistics or blast resistance applications. A composite of the present invention, in some embodiments, comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent, and wherein the composite is adapted for use in ballistics or blast resistance applications. In some embodiments, a composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O, wherein the composite is adapted for use in ballistics or blast resistance applications. In some embodiments, a composite of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4, wherein the composite is adapted for use in ballistics or blast resistance applications. In other embodiments, a composite of the present invention adapted for use in ballistics or blast resistance applications can comprise a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers was formed from one of the other glass compositions disclosed herein as part of the present invention.

Some embodiments of the present invention relate to panels, such as armor panels, comprising composites of the present invention. In some embodiments, a composite of the present invention can be formed into a panel, wherein the panel is expected to exhibit desirable 0.30 cal FSP V50 values (e.g., at least about 900 fps at a panel areal density of about 2 lb/ft² and a panel thickness of about 5-6 mm) when measured by MIL-STD-662F. In other embodiments, a composite of the present invention can be formed into a panel, wherein the panel is expected to exhibit desirable 0.30 cal FSP V50 values (e.g., at least about 1000 fps at a panel areal density of about 2 lb/ft² and a panel thickness of about 5-6 mm) when measured by MIL-STD-662F. In still other embodiments of the present invention, a composite can be formed into a panel, wherein the panel is expected to exhibit desirable 0.30 cal FSP V50 values (e.g., at least about 1100 fps at a panel areal density of about 2 lb/ft² and a panel thickness of about 5-6 mm) when measured MIL-STD-662F. In some embodiments of the present invention, a composite can be formed into a panel, wherein the panel is expected to exhibit desirable 0.30 cal FSP V50 values (e.g., about 900 fps to about 1140 fps at a panel areal density of about 2 lb/ft² and a panel thickness of about 5-6 mm) when measured by MIL-STD-662F.

In some embodiments, a composite of the present invention can be formed into a panel, wherein the panel is expected to exhibit desirable 0.50 cal FSP V50 values (e.g., at least about 1200 fps at a panel areal density of about 4.8-4.9 lb/ft² and a panel thickness of about 13-13.5 mm) when measured by MIL-STD-662F. In other embodiments of the present invention, a composite can be formed into a panel, wherein the panel is expected to exhibit desirable 0.50 cal FSP V50 values (at least about 1300 fps at a panel areal density of about 4.8-4.9 lb/ft² and a panel thickness of about 13-13.5 mm) when measured by MIL-STD-662F. In still other embodiments of the present invention, a composite can be formed into a panel, wherein the panel is expected to exhibit desirable 0.50 cal FSP V50 values (at least about 1400 fps at a panel areal density of about 4.8-4.9 lb/ft² and a panel thickness of about 13-13.5 mm) when measured by MIL-STD-662F. In some embodiments of the present invention, a composite can be formed into a panel, wherein the panel is expected to exhibit desirable 0.50 cal FSP V50 values (e.g., about 1200 fps to about 1440 fps at a panel areal density of about 4.8-4.9 lb/ft² and a panel thickness of about 13-13.5 mm) when measured by MIL-STD-662F.

Composites of the present invention adapted for use in ballistics or blast resistance can comprise various polymeric resins. In some embodiments of the present invention, a composite comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition as disclosed herein, the composite can be formed into a panel, such as an armor panel for ballistic or blast resistance, and the polymeric resin comprises an epoxy resin. A composite of the present invention, in some embodiments, comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition as disclosed herein, the composite can be formed into a panel, such as an armor panel for ballistic or blast resistance, and the polymeric resin comprises a polydicyclopentadiene resin. In some embodiments of the present invention, the polymeric resin can comprise polyethylene, polypropylene, polyamides (including Nylon), polybutylene terephthalate, polycarbonate, thermoplastic polyurethane, phenolic, polyester, vinyl ester, thermoset polyurethane, cyanate esters, or bis-maleimide resins.

Some embodiments of the present invention relate to composites for use in casings for missiles and other explosive delivery devices. In some embodiments, a composite for use in casings for missiles and other explosive delivery devices of the present invention exhibits properties desirable for use in such applications, such as high modulus, high strength, high elongation, low coefficient of thermal expansion, high glass softening temperature, and/or high glass transition temperature.

In some embodiments, a composite for use in casings for missiles and other explosive delivery devices of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). A composite for use in casings for missiles and other explosive delivery devices of the present invention, in some embodiments, comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments a composite for use in casings for missiles and other explosive delivery devices of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments a composite for use in casings for missiles and other explosive delivery devices of the present invention comprises a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4. In other embodiments, a composite for use in casings for missiles and other explosive delivery devices of the present invention can comprise a polymeric resin and a plurality of glass fibers disposed in the polymeric resin, wherein at least one of the plurality of glass fibers was formed from one of the other glass compositions disclosed herein as part of the present invention.

In some embodiments, a composite for use in casings for missiles and other explosive delivery devices of the present invention comprises a polymeric resin and at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In some embodiments, a composite for use in casings for missiles and other explosive delivery devices of the present invention comprises a polymeric resin and at least a portion of a roving comprising at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In other embodiments, a composite for use in casings for missiles and other explosive delivery devices of the present invention comprises a polymeric resin and at least one yarn as disclosed herein disposed in the polymeric resin. In still other embodiments, a composite for use in casings for missiles and other explosive delivery devices of the present invention comprises a polymeric resin and at least one fabric as disclosed herein disposed in the polymeric resin. In some embodiments, a composite for use in casings for missiles and other explosive delivery devices of the present invention comprises at least one fill yarn comprising at least one fiber glass strand as disclosed herein and at least one warp yarn comprising at least one fiber glass strand as disclosed herein.

Composites for use in casings for missiles and other explosive delivery devices of the present invention can comprise various polymeric resins, depending on the desired properties and applications. In some embodiments of the present invention comprising a composite for use in casings for missiles and other explosive delivery devices, the polymeric resin can comprise a thermosetting resin. Examples of common thermosetting resins that can be used in such applications include, without limitation, epoxy, phenolic, polyester, and other thermosetting resins known to those of skill in the art.

While a number of exemplary uses and applications for composites of the present invention are described herein, persons of skill in the art can identify other potential uses for such composites including, for example, other applications in the oil and gas industry, other applications related to transportation and infrastructure, other applications in alternative energy, other high temperature thermal insulation (i.e., thermal shielding) applications (due to higher strength, higher modulus, higher softening temperature and higher glass transition temperature), etc.

Some embodiments of the present invention relate to prepregs. Prepregs of the present invention can comprise a polymeric resin and at least one fiber glass strand as disclosed herein. In some embodiments, a prepreg of the present invention comprises a polymeric resin and a plurality of glass fibers in contact with the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and greater than about 1 weight percent MnO_(x). A prepreg of the present invention, in some embodiments, comprises a polymeric resin and a plurality of glass fibers in contact with the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, from about 0 to about 4 weight percent BaO, from about 0 to about 4 weight percent SrO, and from about 0 to about 5.5 weight percent ZrO, wherein the sum of BaO+SrO+ZnO is greater than about 2 weight percent. In some embodiments, a prepreg of the present invention comprises a polymeric resin and a plurality of glass fibers in contact with the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 11 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and from greater than about 0 to about 2.5 weight percent Cu₂O. In some embodiments, a prepreg of the present invention comprises a polymeric resin and a plurality of glass fibers in contact with the polymeric resin, wherein at least one of the plurality of glass fibers comprises a glass composition that comprises the following components: from about 51 to about 70 weight percent SiO₂, from about 12.5 to about 22 weight percent Al₂O₃, from about 0 to about 20 weight percent CaO, from about 0 to about 12.5 weight percent MgO, from about 0.2 to about 1 weight percent Fe₂O₃, about 0.05 or greater weight percent RE₂O₃, and at least one additional feature selected from the group consisting of La₂O₃ is present in an amount greater than about 2 weight percent, CaO is present in an amount less than about 2 weight percent, a MgO/CaO ratio less than about 1, and a SiO₂/Al₂O₃ ratio greater than about 4. In other embodiments, a prepreg of the present invention can comprise a polymeric resin and a plurality of glass fibers in contact with the polymeric resin, wherein at least one of the plurality of glass fibers was formed from one of the other glass compositions disclosed herein as part of the present invention.

In some embodiments, a prepreg of the present invention comprises a polymeric resin and at least one fiber glass strand as disclosed herein in contact with the polymeric resin. In some embodiments, a prepreg of the present invention comprises a polymeric resin and at least a portion of a roving comprising at least one fiber glass strand as disclosed herein disposed in the polymeric resin. In other embodiments, a prepreg of the present invention comprises a polymeric resin and at least one yarn as disclosed herein in contact with the polymeric resin. In still other embodiments, a prepreg of the present invention comprises a polymeric resin and at least one fabric as disclosed herein in contact with the polymeric resin. In some embodiments, a prepreg of the present invention comprises at least one fill yarn comprising at least one fiber glass strand as disclosed herein and at least one warp yarn comprising at least one fiber glass strand as disclosed herein.

Prepregs of the present invention can comprise various polymeric resins, depending on the desired properties and applications. In some embodiments of the present invention comprising a prepreg, the polymeric resin comprises an epoxy resin. In other embodiments of the present invention comprising a prepreg, the polymeric resin can comprise polyethylene, polypropylene, polyamide, polyimide, polybutylene terephthalate, polycarbonate, thermoplastic polyurethane, phenolic, polyester, vinyl ester, polydicyclopentadiene, polyphenylene sulfide, polyether ether ketone, cyanate esters, bis-maleimides, and thermoset polyurethane resins.

While many of the applications for the glass fibers described herein are reinforcement applications, some embodiments of glass fibers of the present invention can be utilized in electronics applications such as printed circuit boards (“PCB”). More particularly, some embodiments of the present invention relate to glass fiber reinforcements that have electrical properties that permit enhancing performance of a PCB. For example, some embodiments of glass fibers of the present invention can have a dielectric constant (D_(k)) desirable for electronics applications. The dielectric constant of a material (D_(k)), also known as “permittivity,” is a measure of the ability of a material to store electric energy. A material to be used as a capacitor desirably has a relatively high D_(k), whereas a material to be used as part of a PCB substrate desirably has a low D_(k), particularly for high speed circuits. D_(k) is the ratio of the charge that would be stored (i.e., the capacitance) of a given material between two metal plates to the amount of charge that would be stored by a void (air or vacuum) between the same two metal plates. As another example, some embodiments of glass fibers of the present invention can have a coefficient for thermal expansion desirable for electronics applications. Accordingly, some embodiments of the present invention can be used in a variety of electrical applications including, without limitation, printed circuit boards, precursors to printed circuit boards (e.g., fabrics, laminates, prepregs, etc.). In such embodiments, the printed circuit board or other composite to be used in electrical applications can comprise a polymeric resin and a plurality of glass fibers in contact with the polymeric resin, wherein at least one of the plurality of glass fibers was formed from any of the glass compositions disclosed herein as part of the present invention. The polymeric resin can include any of those known to those of skill in the art for use in printed circuit boards or other electrical applications.

Turning now to methods of manufacturing glass fibers of the present invention and related products, glass fibers of the present invention can be prepared in the conventional manner well known in the art, by blending the raw materials used to supply the specific oxides that form the composition of the fibers. Glass fibers according to the various embodiments of the present invention can be formed using any process known in the art for forming glass fibers, and more desirably, any process known in the art for forming essentially continuous glass fibers. For example, although not limiting herein, the glass fibers according to non-limiting embodiments of the present invention can be formed using direct-melt or indirect-melt fiber forming methods. These methods are well known in the art and further discussion thereof is not believed to be necessary in view of the present disclosure. See, e.g., K. L. Loewenstein, The Manufacturing Technology of Continuous Glass Fibers, 3rd Ed., Elsevier, N.Y., 1993 at pages 47-48 and 117-234.

Following formation of the glass fibers, a primary sizing composition can be applied to the glass fibers using any suitable method known to one of ordinary skill in the art. In some embodiments, the sizing composition can be applied immediately after forming the glass fibers. In general, glass fibers used to form fiber glass strands, fabrics, composites, laminates, and prepregs of the present invention will be at least partially coated with a sizing composition. One skilled in the art may choose one of many commercially available sizing compositions for the glass fibers based upon a number of factors including, for example, performance properties of the sizing compositions, desired flexibility of the resulting fabric, cost, and other factors. In some embodiments, the sizing composition does not comprise a starch-oil sizing composition. In some embodiments of the present invention comprising a sizing composition that does not comprise a starch-oil sizing composition, a sized glass fiber or glass fiber strand need not be further treated with a slashing composition prior to using the fiber or strand in weaving applications. In other embodiments comprising a sizing composition that does not comprise a starch-oil sizing composition, a sized glass fiber or glass fiber strand may optionally be further treated with a slashing composition prior to using the fiber or strand in weaving applications. In some embodiments of the present invention comprising a primary sizing composition, the sizing composition can comprise a starch-oil sizing composition. In some embodiments of the present invention comprising a starch-oil sizing composition, the starch-oil sizing composition may later be removed from a fabric formed from at least one sized glass fiber or fiber glass strand. In some embodiments, the starch-oil sizing may be removed from a fabric using any suitable method known to one of ordinary skill in the art, such as but not limited to heat cleaning. In embodiments of the present invention comprising fabrics from which a starch-oil sizing composition has been removed, a fabric of the present invention may further be treated with a finish coating.

Non-limiting examples of commercially available sizing compositions that can be used in some embodiments of the present invention include sizing compositions often used on single-end rovings, such as Hybon 2026, Hybon 2002, Hybon 1383, Hybon 2006, Hybon 2022, Hybon 2032, Hybon 2016, and Hybon 1062, as well as sizing compositions often used on yarns, such as 1383, 611, 900, 610, 695, and 690, each of which refer to sizing compositions for products commercially available from PPG Industries, Inc.

Fiber glass strands of the present invention can be prepared by any suitable method known to one of ordinary skill in the art. Glass fiber fabrics of the present invention can generally be made by any suitable method known to one of ordinary skill in the art, such as but not limited to interweaving weft yarns (also referred to as “fill yarns”) into a plurality of warp yarns. Such interweaving can be accomplished by positioning the warp yarns in a generally parallel, planar array on a loom, and thereafter weaving the weft yarns into the warp yarns by passing the weft yarns over and under the warp yarns in a predetermined repetitive pattern. The pattern used depends upon the desired fabric style.

Warp yarns can generally be prepared using techniques known to those of skill in the art. Warp yarns can be formed by attenuating a plurality of molten glass streams from a bushing or spinner. Thereafter, a sizing composition can be applied to the individual glass fibers and the fibers can be gathered together to form a strand. The strands can be subsequently processed into yarns by transferring the strands to a bobbin via a twist frame. During this transfer, the strands can be given a twist to aid in holding the bundle of fibers together. These twisted strands can then be wound about the bobbin, and the bobbins can be used in the weaving processes.

Positioning of the warp yarns on the loom can generally be done using techniques known to those of ordinary skill in the art. Positioning of the warp yarns on the loom can be done by way of a loom beam. A loom beam comprises a specified number of warp yarns (also referred to as “ends”) wound in an essentially parallel arrangement (also referred to as “warp sheet”) about a cylindrical core. Loom beam preparation can comprise combining multiple yarn packages, each package comprising a fraction of the number of ends required for the loom beam, into a single package or loom beam. For example and although not limiting herein, a 50 inch (127 cm) wide, 7781 style fabric which utilizes a DE75 yarn input typically requires 2868 ends. However, conventional equipment for forming a loom beam does not allow for all of these ends to be transferred from bobbins to a single beam in one operation. Therefore, multiple beams comprising a fraction of the number of required ends, typically referred to as “section beams,” can be produced and thereafter combined to form the loom beam. In a manner similar to a loom beam, a section beam can include a cylindrical core comprising a plurality of essentially parallel warp yarns wound thereabout. While it will be recognized by one skilled in the art that the section beam can comprise any number of warp yarns required to form the final loom beam, generally the number of ends contained on a section beam is limited by the capacity of the warping creel. For a 7781 style fabric, four section beams of 717 ends each of DE75 yarn are typically provided and when combined offer the required 2868 ends for the warp sheet, as discussed above.

Composites of the present invention can be prepared by any suitable method known to one of ordinary skill in the art, such as but not limited to vacuum assisted resin infusion molding, extrusion compounding, compression molding, resin transfer molding, filament winding, prepreg/autoclave curing, and pultrusion. Composites of the present invention can be prepared using such molding techniques as known to those of ordinary skill in the art. In particular, embodiments of composites of the present invention that incorporate woven fiber glass fabrics can be prepared using techniques known to those of skill in the art for preparation of such composites.

As an example, some composites of the present invention can be made using vacuum assisted compression molding, which technique is well-known to those of skill in the art and described briefly below. As known to those of skill in the art, with vacuum assisted compression molding, a stack of pre-impregnated glass fabrics is placed within a press platen. In some embodiments of the present invention, the stack of pre-impregnated glass fabrics can include one or more fabrics of the present invention as described herein that have been cut to a desired size and shape. Upon completion of the stacking operation for the corresponding number of layers, the press is closed and the platens are connected to a vacuum pump so that the upper platen compresses on the stack of fabrics until the desired pressure is achieved. The vacuum aids in the evacuation of entrapped air within the stack and provides for a reduced void content in the molded laminate. Following connection of the platens to a vacuum pump, the temperature of the platens is then increased to accelerate the conversion rate of the resin (e.g., a thermosetting resin) to a predetermined temperature setting particular to the resin utilized, and kept at that temperature and pressure setting until the laminate reaches full cure. At this point, the heat is turned off and the platens are cooled by water circulation until they reach room temperature. The platens can then be opened, and the molded laminate can be removed from the press.

As another example, some composites of the present invention can be made using vacuum assisted resin infusion technology, as further described herein. A stack of glass fiber fabrics of the present invention may be cut to a desired size and placed on a silicone release treated glass table. The stack may then be covered with a peel ply, fitted with a flow enhancing media, and vacuum bagged using nylon bagging film. Next, the so-called “lay up” may be subjected to a vacuum pressure of about 27 inches Hg. Separately, the polymeric resin that is to be reinforced with the fiber glass fabrics can be prepared using techniques known to those of skill in the art for that particular resin. For example, for some polymeric resins, an appropriate resin (e.g., an amine-curable epoxy resin) may be mixed with an appropriate curing agent (e.g., an amine for an amine-curable epoxy resin) in the proportions recommended by the resin manufacturer or otherwise known to a person of ordinary skill in the art. The combined resin may then be degassed in a vacuum chamber for 30 minutes and infused through the fabric preform until substantially complete wet out of the fabric stack is achieved. At this point, the table may be covered with heated blankets (set to a temperature of about 45-50° C.) for 24 hours. The resulting rigid composites may then be de-molded and post cured at about 250° F. for 4 hours in a programmable convection oven. As is known to persons of ordinary skill in the art, however, various parameters such as degassing time, heating time, and post curing conditions may vary based on the specific resin system used, and persons of ordinary skill in the art understand how to select such parameters based on a particular resin system.

Prepregs of the present invention can be prepared by any suitable means known to one of ordinary skill in the art, such as but not limited to passing fiber glass strands, rovings, or fabrics through a resin bath; using a solvent-based resin; or using a resin film.

As noted above, composites of the present invention can comprise a polymeric resin, in some embodiments. A variety of polymeric resins can be used. Polymeric resins that are known to be useful in reinforcement applications can be particularly useful in some embodiments. In some embodiments, the polymeric resin can comprise a thermoset resin. Thermoset resin systems useful in some embodiments of the present invention can include but are not limited to epoxy resin systems, phenolic based resins, polyesters, vinyl esters, thermoset polyurethanes, polydicyclopentadiene (pDCPD) resins, cyanate esters, and bis-maleimides. In some embodiments, the polymeric resin can comprise an epoxy resin. In other embodiments, the polymeric resin can comprise a thermoplastic resin. Thermoplastic polymers useful in some embodiments of the present invention include but are not limited to polyethylene, polypropylene, polyamides (including Nylon), polybutylene terephthalate, polycarbonate, thermoplastic polyurethanes (TPU), polyphenylene sulfides, and polyether ether keteone (PEEK). Non-limiting examples of commercially available polymeric resins useful in some embodiments of the present invention include EPIKOTE Resin MGS® RIMR 135 epoxy with Epikure MGS RIMH 1366 curing agent (available from Momentive Specialty Chemicals Inc. of Columbus, Ohio), Applied Poleramic MMFCS2 epoxy (available from Applied Poleramic, Inc., Benicia, Calif.), and EP255 modified epoxy (available from Barrday Composite Solutions, Millbury, Mass.).

The invention will be illustrated through the following series of specific embodiments. However, it will be understood by one of skill in the art that many other embodiments are contemplated by the principles of the invention.

EXAMPLES

Table 1 provides a plurality of fiberizable glass compositions according to various embodiments of the present invention as well as data relating to various properties of such compositions. Examples 1, 20, 21, 25, 62, and 77 are comparative examples, while the remaining examples represent various embodiments of the present invention.

The glasses in these examples were made by melting mixtures of commercial and reagent grade chemicals (reagent grade chemicals were used only for the rare earth oxides) in powder form in 10% Rh/Pt crucibles at the temperatures between 1500° C. and 1550° C. (2732° F.-2822° F.) for four hours. Each batch was about 1000 grams. After the 4 hour melting period, the molten glass was poured onto a steel plate for quenching. Volatile species, such as fluoride and alkali oxides, were not adjusted in the batches for their emission loss because of their low concentrations in the glasses. The compositions in the Examples represent as-batched compositions. Commercial ingredients were used in preparing the glasses. In the batch calculation, special raw material retention factors were considered to calculate the oxides in each glass. The retention factors are based on years of glass batch melting and oxides yield in the glass as measured. Hence, the as-batched compositions illustrated in the examples are considered to be close to the measured compositions.

Melt Properties

Melt viscosity as a function of temperature and liquidus temperature was determined by using ASTM Test Method C965 “Standard Practice for Measuring Viscosity of Glass Above the Softening Point,” and C829 “Standard Practices for Measurement of Liquidus Temperature of Glass by the Gradient Furnace Method,” respectively.

Table 1 includes measured liquidus temperature (T_(L)), reference temperature of forming (T_(F)) defined by melt viscosity of 1000 Poise, and reference temperature of melting (T_(m)) defined by viscosity of 100 Poise, for the glass compositions. The difference between the forming temperature and the liquidus temperature (ΔT) is also shown. Table 1 also provides softening temperatures (T_(soft)), glass transition temperatures (T_(g)), and coefficients of thermal expansion (CTE) for some of the compositions. Softening temperature (T_(soft)) values were measured in accordance with ASTM Test Method C338-93 “Standard Test Method for Softening Point of Glass” (2008). Glass transition temperature (T_(g)) values were measured in accordance with ASTM Test Method C336-71 “Annealing Point and Strain Point by Fiber Elongation.” Coefficient of thermal expansion (CTE) values were determined in accordance with ASTM E228-11 “Standard Test Method for Linear Thermal Expansion of Solid Materials with a Push-Rod Dilatometer.”

Mechanical Properties

For the fiber tensile strength test, fiber samples from the glass compositions were produced from a 10Rh/90Pt single tip fiber drawing unit. Approximately, 85 grams of cullet of a given composition was fed into the bushing melting unit and conditioned at a temperature close or equal to the 100 Poise melt viscosity for two hours. The melt was subsequently lowered to a temperature close or equal to the 1000 Poise melt viscosity and stabilized for one hour prior to fiber drawing. Fiber diameter was controlled to produce an approximately 10 μm diameter fiber by controlling the speed of the fiber drawing winder. All fiber samples were captured in air without any contact with foreign objects. The fiber drawing was completed in a room with a controlled humidity of between 40 and 45% RH.

Fiber tensile strength was measured using a Kawabata KES-G1 (Kato Tech Co. Ltd., Japan) tensile strength analyzer equipped with a Kawabata type C load cell. Fiber samples were mounted on paper framing strips using a resin adhesive. A tensile force was applied to the fiber until failure, from which the fiber strength was determined based on the fiber diameter and breaking stress. The test was done at room temperature under the controlled humidity between 40-45% RH. The average values were computed based on a sample size of 65-72 fibers for each composition. Table 1 reports the average tensile strengths for fibers formed from some of the compositions. Specific strengths were calculated by dividing the tensile strength values (in N/m²) by the corresponding densities (in g/m³).

Young's modulus was also measured for certain glass compositions in Table 1 using the following technique. Approximately 50 grams of glass cullet having a composition corresponding to the appropriate example Table 1 was re-melted in a 90Pt/10Rh crucible for two hours at a melting temperature defined by 100 Poise. The crucible was subsequently transferred into a vertical tube, electrically heated furnace. The furnace temperature was preset at a fiber pulling temperature close or equal to a 1000 Poise melt viscosity. The glass was equilibrated at the temperature for one hour before fiber drawing. The top of the fiber drawing furnace had a cover with a center hole, above which a water-cooled copper coil was mounted to regulate the fiber cooling. A silica rod was then manually dipped into the melt through the cooling coil, and a fiber about 1-1.5 m long was drawn out and collected. The diameter of the fiber ranged from 100μ at one end to 1000 μm at the other end.

Elastic moduli were determined using an ultrasonic acoustic pulse technique (Panatherm 5010 unit from Panametrics, Inc. of Waltham, Mass.) for the fibers drawn from the glass melts. Extensional wave reflection time was obtained using twenty micro-second duration, 200 kHz pulses. The sample length was measured and the respective extensional wave velocity (V_(E)) was calculated. Fiber density (p) was measured using a Micromeritics AccuPyc 1330 pycnometer. About 20 measurements were made for each composition and the average Young's modulus (E) was calculated from the following formula: E=V _(E) ²×ρ The modulus tester uses a wave guide with a diameter of 1 mm, which sets the fiber diameter at the contact side with the wave guide to be about the same as the wave guide diameter. In other words, the end of the fiber having a diameter of 1000 μm was connected at the contact side of the wave guide. Fibers with various diameters were tested for Young's modulus and the results show that a fiber diameter from 100 to 1000 μm does not affect fiber modulus. Specific modulus values were calculated by dividing the Young's modulus values by the corresponding densities.

The values of “Fiber Failure strain (%)” (i.e., fiber elongation) in Table 1 were determined based on Hooke's law by dividing the tensile strength values by the corresponding Young's modulus values (in the same units (e.g., all in MPa)), and multiplying by 100.

TABLE 1 1 2 3 4 5 6 SiO₂ 61.49 61.46 61.37 61.46 61.37 61.46 Al₂O₃ 15.28 15.36 15.57 15.36 15.57 15.36 Fe₂O₃ 0.29 0.29 0.29 0.29 0.29 0.29 CaO 15.43 13.18 12.51 13.18 12.51 13.18 MgO 6.12 6.26 6.21 6.26 6.21 6.26 Na₂O 0.05 0.05 0.05 0.05 0.05 0.05 K₂O 0.09 0.09 0.09 0.09 0.09 0.09 Sc₂O₃ 0.00 2.08 2.68 0.00 0.00 0.00 Y₂O₃ 0.00 0.00 0.00 2.08 2.68 0.00 La₂O₃ 0.00 0.00 0.00 0.00 0.00 2.08 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.50 0.50 0.51 0.50 0.51 0.50 Li₂O 0.74 0.72 0.72 0.72 0.72 0.72 SO₃ 0.01 0.01 0.01 0.01 0.01 0.01 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 T_(L) (° C.) 1198 1197 1241 1197 1201 1199 T_(F) (° C.) 1285 1288 1296 1306 1312 1300 ΔT (° C.) 87 91 55 109 111 101 T_(m) (° C.) 1489 1485 1495 1509 1513 1507 Fiber Density 2.62 2.62 2.62 2.62 2.63 2.63 (g/cm³) Fiber Modulus 89.2 91.0 91.6 90.6 90.2 88.0 (GPa) Fiber Strength 3570 4108 4376 4264 4727 4321 (MPa) Fiber Failure 4.0 4.5 4.8 4.7 5.2 4.9 Strain (%) Specific Fiber 3.5 3.6 3.6 3.5 3.5 3.4 Modulus (×10⁶ m) Specific Fiber 139 160 171 166 184 168 Strength (×10³ m) 7 8 9 10 11 12 SiO₂ 61.37 61.46 61.37 59.74 59.73 59.73 Al₂O₃ 15.57 15.36 15.57 16.00 17.46 17.46 Fe₂O₃ 0.29 0.29 0.29 0.27 0.29 0.29 CaO 12.51 13.18 12.51 9.63 7.46 7.46 MgO 6.21 6.26 6.21 8.58 7.13 7.13 Na₂O 0.05 0.05 0.05 0.19 0.19 0.19 K₂O 0.09 0.09 0.09 0.09 0.09 0.09 Sc₂O₃ 0.00 0.00 0.00 4.24 6.34 4.44 Y₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 2.68 0.00 0.00 0.00 0.00 1.90 Nd₂O₃ 0.00 2.08 2.68 0.00 0.00 0.00 TiO₂ 0.51 0.50 0.51 0.63 0.69 0.69 Li₂O 0.72 0.72 0.72 0.61 0.61 0.61 SO₃ 0.01 0.01 0.01 0.02 0.02 0.02 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 T_(L) (° C.) 1198 1201 1201 1355 1376 T_(F) (° C.) 1309 1300 1308 1308 1349 1315 ΔT (° C.) 111 99 107 −47 −61 T_(m) (° C.) 1515 1506 1513 1491 1515 1507 Fiber Density 2.63 2.62 2.62 2.63 (g/cm³) Fiber Modulus 88.4 88.1 88.9 92.1 (GPa) Fiber Strength 4639 (MPa) Fiber Failure 5.3 Strain (%) Specific Fiber 3.4 3.4 3.5 3.6 Modulus (×10⁶ m) Specific Fiber 180 Strength (×10³ m) 13 14 15 16 17 18 SiO₂ 59.73 59.74 59.73 59.73 59.73 59.73 Al₂O₃ 17.46 16.00 17.46 17.46 17.46 17.46 Fe₂O₃ 0.29 0.27 0.29 0.29 0.29 0.29 CaO 7.46 9.63 7.46 7.46 7.46 7.46 MgO 7.13 8.58 7.13 7.13 7.13 7.13 Na₂O 0.19 0.19 0.19 0.19 0.19 0.19 K₂O 0.09 0.09 0.09 0.09 0.09 0.09 Sc₂O₃ 3.17 0.00 0.00 0.00 0.00 4.44 Y₂O₃ 0.00 4.24 6.34 4.44 3.17 0.00 La₂O₃ 3.17 0.00 0.00 1.90 3.17 0.00 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.69 0.63 0.69 0.69 0.69 2.59 Li₂O 0.61 0.61 0.61 0.61 0.61 0.61 SO₃ 0.02 0.02 0.02 0.02 0.02 0.02 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 T_(L) (° C.) 1302 1194 1194 1193 1197 T_(F) (° C.) 1317 1287 1327 1326 1330 ΔT (° C.) 15 93 133 133 133 T_(m) (° C.) 1512 1476 1515 1523 1532 Fiber Density 2.64 2.65 2.65 2.65 2.65 (g/cm³) Fiber Modulus 91.8 92.1 92.2 91.5 91.9 (GPa) Fiber Strength 5255 5181 5195 (MPa) Fiber Failure 5.7 5.7 5.7 Strain (%) Specific Fiber 3.5 3.5 3.5 3.5 3.5 Modulus (×10⁶ m) Specific Fiber 202 199 200 Strength (×10³ m) 19 20 21 22 23 24 SiO₂ 59.73 60.31 60.22 59.85 59.85 60.37 Al₂O₃ 17.46 15.62 16.28 15.58 15.58 14.48 Fe₂O₃ 0.29 0.23 0.28 0.27 0.27 0.25 CaO 7.46 13.84 13.06 11.05 11.05 5.46 MgO 7.13 8.63 8.61 8.70 8.70 8.03 Na₂O 0.19 0.06 0.06 0.20 0.20 0.18 K₂O 0.09 0.07 0.09 0.09 0.09 0.08 Sc₂O₃ 4.44 0.00 0.00 2.88 0.00 0.00 Y₂O₃ 0.00 0.00 0.00 0.00 2.88 0.00 La₂O₃ 0.00 0.00 0.00 0.00 0.00 9.87 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.69 0.45 0.64 0.61 0.61 0.57 Li₂O 0.61 0.78 0.75 0.76 0.76 0.70 SO₃ 0.02 0.02 0.02 0.02 0.02 0.01 ZrO₂ 1.90 0.00 0.00 0.00 0.00 0.00 B₂O₃ TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 T_(L) (° C.) 1211 1225 1240 1195 1260 T_(F) (° C.) 1251 1265 1264 1268 1320 ΔT (° C.) 40 40 24 73 60 T_(m) (° C.) 1441 1457 1450 1458 1523 Fiber Density 2.62 2.62 2.64 2.64 2.70 (g/cm³) Fiber Modulus 90.2 90.5 92.4 91.1 89.5 (GPa) Fiber Strength 4622 4739 4913 4759 4978 (MPa) Fiber Failure 5.13 5.2 5.3 5.2 5.6 Strain (%) Specific Fiber 3.51 3.5 3.6 3.5 3.4 Modulus (×10⁶ m) Specific Fiber 180 185 190 184 188 Strength (×10³ m) 25 26 27 28 29 30 SiO₂ 59.54 59.73 59.77 62.85 54.20 59.94 Al₂O₃ 17.28 17.35 17.36 19.78 15.20 15.66 Fe₂O₃ 0.30 0.29 0.28 0.32 0.26 0.25 CaO 9.68 4.99 0.69 2.77 6.41 13.03 MgO 11.28 11.25 11.20 7.00 6.73 7.80 Na₂O 1.12 1.12 1.12 2.40 0.03 0.03 K₂O 0.10 0.09 0.09 0.00 0.07 0.09 Sc₂O₃ 0.00 0.00 0.00 3.16 3.88 0.00 Y₂O₃ 0.00 0.00 0.00 0.00 0.00 1.99 La₂O₃ 0.00 4.49 8.78 0.00 3.88 0.00 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.68 0.68 0.68 0.78 0.02 0.52 Li₂O 0.00 0.00 0.00 0.00 0.59 0.65 SO₃ 0.02 0.02 0.02 0.02 0.02 0.02 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.93 8.71 0 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 T_(L) (° C.) 1265 1268 1324 1344 1300 1211 T_(F) (° C.) 1285 1316 1361 1397 1414 1275 ΔT (° C.) 20 48 37 53 114 64 T_(m) (° C.) 1471 1508 1559 1613 1631 1466 Fiber Density 2.61 2.64 2.67 2.51 2.53 2.64 (g/cm³) Fiber Modulus 90.0 90.5 90.1 87.1 85.9 90.4 (GPa) Fiber Strength 5105 5294 5445 5503 5492 (MPa) Fiber Failure 5.7 5.9 6.0 6.3 6.4 Strain (%) Specific Fiber 3.5 3.5 3.4 3.5 3.5 3.5 Modulus (×10⁶ m) Specific Fiber 199.7 204.8 208.0 223.4 221.8 Strength (×10³ m) 31 32 33 34 35 36 SiO₂ 59.94 59.94 60.85 61.67 61.67 59.52 Al₂O₃ 15.66 15.66 15.90 16.33 16.33 17.24 Fe₂O₃ 0.25 0.25 0.25 0.26 0.26 0.27 CaO 13.03 13.03 13.23 6.01 6.01 6.35 MgO 7.80 7.80 7.92 10.26 10.26 10.85 Na₂O 0.03 0.03 0.03 0.16 0.16 0.17 K₂O 0.09 0.09 0.10 0.09 0.09 0.10 Sc₂O₃ 0.00 1.99 0.51 0.00 0.00 0.00 Y₂O₃ 0.00 0.00 0.00 4.21 0.00 4.44 La₂O₃ 1.99 0.00 0.00 0.00 4.21 0.00 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.52 0.52 0.53 0.58 0.58 0.61 Li₂O 0.65 0.65 0.66 0.42 0.42 0.44 SO₃ 0.02 0.02 0.02 0.00 0.00 0.00 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0 0 0 0 0 0 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 T_(L) (° C.) 1209 1212 1213 1258 1247 1232 T_(F) (° C.) 1265 1263 1270 1329 1331 1300 ΔT (° C.) 56 51 57 71 84 68 T_(m) (° C.) 1458 1451 1466 1529 1535 1489 Fiber Density 2.64 2.64 2.62 2.62 2.65 (g/cm³) Fiber Modulus 90.6 90.3 92.2 90.9 94.1 (GPa) Fiber Strength 5224 (MPa) Fiber Failure 5.6 Strain (%) Specific Fiber 3.5 3.5 3.6 3.5 3.6 Modulus (×10⁶ m) Specific Fiber 201 Strength (×10³ m) 37 38 39 40 41 42 SiO₂ 59.52 59.00 59.52 60.36 59.84 61.69 Al₂O₃ 17.24 17.25 17.40 17.65 18.14 21.64 Fe₂O₃ 0.27 0.29 0.29 0.29 0.30 0.34 CaO 6.35 6.18 5.37 4.05 3.57 1.01 MgO 10.85 10.65 10.73 10.86 11.85 10.12 Na₂O 0.17 0.02 0.02 0.02 0.02 0.02 K₂O 0.10 0.09 0.09 0.09 0.09 0.11 Sc₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 0.00 5.84 5.90 5.98 5.47 4.21 La₂O₃ 4.44 0.00 0.00 0.00 0.00 0.00 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.61 0.68 0.68 0.69 0.71 0.85 Li₂O 0.44 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 T_(L) (° C.) 1237 1276 1297 1336 1316 T_(F) (° C.) 1302 1315 1324 1340 1332 1392 ΔT (° C.) 65 39 27 4 16 T_(m) (° C.) 1496 1500 1509 1529 1518 1599 T_(soft) (° C.) 951 958 978 962 995 CTE (10⁻⁶/° C.) 3.1 Fiber Density 2.66 2.63 2.66 2.65 2.65 2.58 (g/cm³) Fiber Modulus 92.8 92.8 93.2 94.1 93.6 92.4 (GPa) Fiber Strength 5076 (MPa) Fiber Failure 5.5 Strain (%) Specific Fiber 3.6 3.6 3.6 3.6 3.6 3.6 Modulus (×10⁶ m) Specific Fiber 197 Strength (×10³ m) 43 44 45 46 47 48 SiO₂ 61.69 60.82 60.82 59.40 60.03 60.48 Al₂O₃ 21.64 21.34 21.34 17.25 17.40 17.67 Fe₂O₃ 0.34 0.34 0.34 0.25 0.26 0.26 CaO 1.01 0.99 0.99 5.78 5.93 4.95 MgO 10.12 9.98 9.98 10.78 10.83 10.64 Na₂O 0.02 0.02 0.02 0.05 0.04 0.04 K₂O 0.11 0.11 0.11 0.10 0.10 0.10 Sc₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 0.00 5.56 0.00 4.79 4.03 4.34 La₂O₃ 4.21 0.00 5.56 0.00 0.00 0.00 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.85 0.84 0.84 0.52 0.57 0.56 Li₂O 0.00 0.00 0.00 1.06 0.81 0.95 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 T_(L) (° C.) 1235 1237 1232 T_(F) (° C.) 1401 1397 1390 1273 1289 1299 ΔT (° C.) 38 52 67 T_(soft) (° C.) 992 993 990 T_(m) (° C.) 1603 1595 1589 1467 1484 1499 Fiber Density 2.58 2.60 2.61 2.65 2.64 2.63 (g/cm³) Fiber Modulus 91.6 92.7 92.0 94.7 93.8 93.1 (GPa) Fiber Strength 5307 5237 5357 (MPa) Fiber Failure 5.6 5.6 5.8 Strain (%) Specific Fiber 3.6 3.6 3.6 3.6 3.6 3.6 Modulus (×10⁶ m) Specific Fiber 204 203 207 Strength (×10³ m) Dielectric 5.69 5.82 5.87 Constant @1 GHz Dissipation loss @ 0.0020 0.0018 0.0017 1 GHz 49 50 51 52 53 54 SiO₂ 59.90 56.85 54.76 57.72 60.07 59.40 Al₂O₃ 16.54 15.70 15.12 16.67 17.56 17.25 Fe₂O₃ 0.24 0.23 0.22 0.22 0.22 0.25 CaO 5.38 5.10 4.92 4.63 4.65 5.78 MgO 11.55 10.96 10.56 9.94 9.97 10.78 Na₂O 0.05 0.04 0.04 0.06 0.07 0.05 K₂O 0.10 0.09 0.09 0.11 0.12 0.10 Sc₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 4.71 9.56 12.89 8.67 4.88 2.40 La₂O₃ 0.00 0.00 0.00 0.00 0.00 2.40 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.50 0.48 0.46 0.43 0.39 0.52 Li₂O 1.03 0.98 0.94 1.55 2.08 1.06 SO₃ 0.00 0.00 0.00 0.00 0.00 0.01 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.01 T_(L) (° C.) 1252 1223 1225 1201 1216 1240 T_(F) (° C.) 1273 1247 1232 1252 1262 1273 ΔT (° C.) 21 24 7 51 46 33 T_(m) (° C.) 1464 1427 1403 1441 1465 1467 Fiber Density 2.65 2.74 2.81 2.71 (g/cm³) Fiber Modulus 93.8 96.4 97.6 95.3 (GPa) Fiber Strength 5013 (MPa) Fiber Failure 5.3 Strain (%) Specific Fiber 3.6 3.6 3.5 3.6 Modulus (×10⁶ m) Specific Fiber 182 Strength (×10³ m) 55 56 57 58 59 60 SiO₂ 59.40 60.03 60.03 60.16 60.16 59.43 Al₂O₃ 17.25 17.40 17.40 18.32 18.32 18.10 Fe₂O₃ 0.25 0.26 0.26 0.28 0.28 0.27 CaO 5.78 5.93 5.93 5.43 5.43 5.36 MgO 10.78 10.83 10.83 10.19 10.19 10.07 Na₂O 0.05 0.04 0.04 0.04 0.04 0.04 K₂O 0.10 0.10 0.10 0.11 0.11 0.10 Sc₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 0.00 2.02 0.00 4.09 0.00 0.00 La₂O₃ 4.79 2.02 4.03 0.00 4.09 5.25 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.52 0.57 0.57 0.61 0.61 0.60 Li₂O 1.06 0.81 0.81 0.79 0.79 0.78 SO₃ 0.01 0.01 0.01 0.00 0.00 0.00 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.01 100.00 100.00 100.00 100.00 T_(L) (° C.) 1245 1240 1245 1233 1233 1227 T_(F) (° C.) 1275 1288 1290 1305 1302 1298 ΔT (° C.) 30 48 45 71 69 71 T_(m) (° C.) 1473 1483 1487 1503 1503 1495 Fiber Density 2.64 2.64 2.63 2.63 2.65 (g/cm³) Fiber Modulus 93.1 92.9 92.8 91.4 91.6 (GPa) Fiber Strength 5368 (MPa) Fiber Failure 5.8 Strain (%) Specific Fiber 3.60 3.6 Modulus (×10⁶ m) Specific Fiber 207 Strength (×10³ m) 61 62 63 64 65 66 SiO₂ 59.99 60.51 60.39 60.20 59.60 58.69 Al₂O₃ 17.86 15.46 15.43 15.39 15.23 15.00 Fe₂O₃ 0.27 0.26 0.26 0.26 0.25 0.25 CaO 4.49 14.49 14.46 14.42 14.27 14.05 MgO 9.92 8.17 8.15 8.13 8.05 7.93 Na₂O 0.04 0.03 0.03 0.03 0.03 0.03 K₂O 0.10 0.09 0.09 0.09 0.09 0.09 Sc₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 0.00 0.00 0.20 0.50 1.50 3.00 La₂O₃ 5.97 0.00 0.00 0.00 0.00 0.00 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.59 0.55 0.54 0.54 0.54 0.53 Li₂O 0.77 0.43 0.43 0.43 0.43 0.42 SO₃ 0.00 0.01 0.01 0.01 0.01 0.01 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 99.99 99.99 99.99 99.99 99.99 T_(L) (° C.) 1240 1205 1208 1200 1202 1209 T_(F) (° C.) 1316 1273 1268 1271 1269 1256 ΔT (° C.) 76 68 60 71 67 47 T_(m) (° C.) 1518 1468 1462 1465 1459 1440 Fiber Density 2.65 2.63 (g/cm³) Fiber Modulus 91.8 89.5 (GPa) Fiber Strength (MPa) Fiber Failure Strain (%) Specific Fiber 3.5 Modulus (×10⁶ m) Specific Fiber Strength (×10³ m) 67 68 69 70 71 72 SiO₂ 58.08 57.48 56.27 60.39 60.20 59.60 Al₂O₃ 14.84 14.69 14.38 15.43 15.39 15.23 Fe₂O₃ 0.25 0.24 0.24 0.26 0.26 0.25 CaO 13.91 13.76 13.47 14.46 14.42 14.27 MgO 7.84 7.76 7.60 8.15 8.13 8.05 Na₂O 0.03 0.03 0.03 0.03 0.03 0.03 K₂O 0.09 0.09 0.09 0.09 0.09 0.09 Sc₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 4.00 5.00 7.00 0.00 0.00 0.00 La₂O₃ 0.00 0.00 0.00 0.20 0.50 1.50 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.52 0.52 0.51 0.54 0.54 0.54 Li₂O 0.42 0.41 0.40 0.43 0.43 0.43 SO₃ 0.01 0.01 0.01 0.01 0.01 0.01 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 99.99 100.00 100.00 99.99 99.99 99.99 T_(L) (° C.) 1206 1208 1212 1207 1205 1204 T_(F) (° C.) 1260 1255 1244 1265 1265 1259 ΔT (° C.) 54 47 32 58 60 55 T_(m) (° C.) 1444 1463 1480 1456 1457 1447 Fiber Density (g/cm³) Fiber Modulus (GPa) Fiber Strength (MPa) Fiber Failure Strain (%) Specific Fiber Modulus (×10⁶ m) Specific Fiber Strength (×10³ m) 73 74 75 76 77 78 79 80 SiO₂ 58.69 58.08 57.48 56.27 60.72 60.81 58.91 58.91 Al₂O₃ 15.00 14.84 14.69 14.38 15.57 13.01 16.95 16.95 Fe₂O₃ 0.25 0.25 0.24 0.24 0.27 0.23 0.25 0.25 CaO 14.05 13.91 13.76 13.47 22.52 19.17 4.35 4.35 MgO 7.93 7.84 7.76 7.60 0.19 0.16 10.49 10.49 Na₂O 0.03 0.03 0.03 0.03 0.01 0.01 0.04 0.04 K₂O 0.09 0.09 0.09 0.09 0.08 0.07 0.10 0.10 Sc₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 0.00 0.00 0.00 0.00 0.00 6.01 3.98 0.00 La₂O₃ 3.00 4.00 5.00 7.00 0.00 0.00 0.00 3.98 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.53 0.52 0.52 0.51 0.63 0.53 2.09 2.09 Li₂O 0.42 0.42 0.41 0.40 0.00 0.00 0.78 0.78 SO₃ 0.01 0.01 0.01 0.01 0.00 0.00 0.00 0.00 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 2.05 2.05 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 99.99 99.99 100.00 100.00 100.00 100.00 100.00 100.00 T_(L) (° C.) 1202 1199 1196 1231 1272 T_(F) (° C.) 1253 1248 1245 1325 1346 1297 1298 ΔT (° C.) 51 49 49 94 74 T_(m) (° C.) 1440 1432 1427 1528 1543 1491 1496 T_(soft) (° C.) 943 962 912 904 T_(g) (° C.) 722 716 CTE (10⁻⁶/° C.) 4.11 4.13 Fiber Density 2.62 2.68 2.66 2.66 (g/cm³) Fiber Modulus 82.0 83.7 93.8 92.4 (GPa) Fiber Strength 3948 4029 (MPa) Fiber Failure 4.8 4.8 Strain (%) Specific Fiber 3.2 3.2 3.6 3.5 Modulus (×10⁶ m) Specific Fiber 154 153 Strength (×10³ m) 81 82 83 84 85 86 87 88 89 SiO₂ 61.43 59.81 59.04 58.66 57.41 58.17 54.56 56.41 51.18 Al₂O₃ 15.14 14.74 14.55 14.45 14.15 14.33 13.44 13.90 12.61 Fe₂O₃ 0.26 0.26 0.25 0.25 0.25 0.25 0.23 0.24 0.22 CaO 14.70 12.52 11.46 10.95 10.72 12.17 9.36 11.80 8.78 MgO 7.98 7.77 7.67 7.62 7.45 7.55 7.08 7.32 6.65 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Sc₂O₃ 0.00 4.43 6.56 7.60 9.56 0.00 0.00 0.00 0.00 Y₂O₃ 0.00 0.00 0.00 0.00 0.00 7.05 14.88 0.00 0.00 La₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 9.87 20.15 Nd₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 0.49 0.48 0.47 0.47 0.46 0.47 0.44 0.45 0.41 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 ZrO₂ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 T_(L) (° C.) 1199 1337 1434 1462 1516 1204 1294 1184 1158 T_(F) (° C.) 1296 1285 1284 1307 1348 1280 1260 1266 1237 ΔT (° C.) 97 −52 −150 −155 −168 76 −34 82 79 T_(m) (° C.) 1495 1471 1458 1447 1449 1464 1426 1450 1406 T_(soft) (° C.) 898 917 920 925 931 911 922 899 903 T_(g) (° C.) 717 740 750 759 757 734 748 721 729 CTE (10⁻⁶/° C.) 4.63 4.61 4.54 4.54 4.44 Fiber Density 2.60 2.64 2.70 2.78 (g/cm³) Fiber Modulus 89.4 92.4 91.6 90.8 (GPa) Fiber Strength (MPa) Fiber Failure Strain (%) Specific Fiber 3.5 3.6 3.5 3.3 Modulus (×10⁶ m) Specific Fiber Strength (×10³ m) 90 91 92 93 SiO₂ 63.08 65.03 65.03 64.49 Al₂O₃ 16.16 15.35 15.35 14.61 Fe₂O₃ 0.24 0.23 0.23 0.19 CaO 4.40 3.37 3.37 3.00 MgO 10.63 10.86 10.86 9.67 Na₂O 0.04 0.04 0.04 0.03 K₂O 0.09 0.09 0.09 0.08 Sc₂O₃ 0.00 0.00 0.00 0.00 Y₂O₃ 0.00 0.00 3.68 0.00 La₂O₃ 4.04 3.68 0.00 4.33 Nd₂O₃ 0.00 0.00 0.00 0.00 TiO₂ 0.52 0.47 0.47 0.39 Li₂O 0.79 0.89 0.89 0.79 SO₃ 0.00 0.00 0.00 0.00 ZrO₂ 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 P₂O₅ 0.00 0.00 0.00 2.42 TOTAL 100.0 100.0 100.0 100.0 T_(L) (° C.) 1267 T_(F) (° C.) 1332 1355 1350 1396 ΔT (° C.) 65 T_(m) (° C.) 1542 1572 1562 1619 Fiber Density 2.60 (g/cm³) Fiber Modulus 91.4 (GPa) Fiber Strength (MPa) Fiber Failure Strain (%) Specific Fiber 3.6 Modulus (×10⁶ m) Specific Fiber Strength (×10³ m)

Certain of these data were plotted in FIGS. 1-4. FIG. 1 is a chart showing Young's modulus values relative to the amount of rare earth oxides (RE₂O₃) for the glass compositions in Examples 1-17, 22, and 23. FIG. 2 is a chart showing pristine fiber tensile strength values relative to the amount of rare earth oxides (RE₂O₃) for the glass compositions in Examples 1-17, 22, and 23. FIG. 3 is a chart showing softening and glass transition temperatures relative to the amount of rare earth oxides (RE₂O₃) for the glass compositions of Examples 81-89. FIG. 4 is a chart showing linear coefficient of thermal expansion relative to the amount of scandium oxide (Sc₂O₃) for the glass compositions of Examples 81-89.

Table 2 provides a plurality of fiberizable glass compositions according to various embodiments of the present invention as well as data relating to various properties of such compositions. The embodiments of Table 2 were produced in the same manner as those in Table 1. The melt properties and mechanical properties of the embodiments of Table 2 were determined in the same manner as for those in Table 1.

TABLE 2 94 95 96 97 98 99 SiO₂ 61.42 60.85 60.07 61.02 61.28 60.18 Al₂O₃ 17.85 17.62 17.52 17.80 17.87 16.77 CaO 5.42 5.64 5.92 6.00 6.01 7.18 MgO 8.81 9.18 9.63 8.22 6.29 8.05 BaO 0.00 0.00 0.00 0.00 0.00 0.00 SrO 0.00 0.00 0.00 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.04 0.05 0.04 0.04 0.04 0.04 K₂O 0.11 0.10 0.10 0.11 0.11 0.10 Li₂O 0.96 1.00 0.91 0.93 0.93 1.01 Fe₂O₃ 0.37 0.37 0.37 0.38 0.38 0.37 TiO₂ 0.56 0.55 0.56 0.57 2.13 1.36 Y₂O₃ 4.45 4.64 4.87 4.94 4.96 4.93 La₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Cu₂O 0.00 0.00 0.00 0.00 0.00 0.00 MnO 0.00 0.00 0.00 0.00 0.00 0.00 MnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 3.44 3.45 3.43 3.43 3.43 3.59 MgO/CaO 1.63 1.63 1.63 1.37 1.05 1.12 CaO + MgO + 14.23 14.82 15.55 14.21 12.29 15.24 BaO + SrO BaO + SrO + ZnO 0.00 0.00 0.00 0.00 0.00 0.00 T_(L) (° C.) 1188 1188 1200 1185 1208 1154 T_(F) (° C.) 1319 1307 1297 1320 1338 1294 ΔT (° C.) 131 119 97 135 130 140 T_(m) (° C.) 1522 1508 1494 1521 1549 1493 Fiber Density 2.61 2.62 2.63 2.62 2.61 (g/cm³) Fiber Modulus (GPa) 92.3 92.0 92.8 91.9 90.0 Fiber Strength (MPa) 5490 5492 5340 5467 Fiber Failure Strain (%) 5.9 6.0 5.8 5.9 Specific Fiber 3.6 3.6 3.6 3.6 3.5 Modulus (×10⁶ m) Specific Fiber 215.0 214.2 207.0 213.2 0.0 Strength (×10³ m) 100 101 102 103 104 105 SiO₂ 61.28 60.18 60.83 60.12 59.78 61.00 Al₂O₃ 17.87 16.77 15.23 17.84 17.99 16.75 CaO 6.01 7.18 7.90 5.88 5.93 4.67 MgO 6.29 8.05 8.86 9.47 9.55 10.20 BaO 0.00 0.00 0.00 0.00 0.00 0.00 SrO 0.00 0.00 0.00 0.00 0.00 2.46 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.04 0.04 0.04 0.04 0.04 0.04 K₂O 0.11 0.10 0.09 0.10 0.10 0.10 Li₂O 0.93 1.01 0.77 0.77 0.78 0.72 Fe₂O₃ 0.38 0.37 0.37 0.39 0.40 0.25 TiO₂ 0.56 0.56 1.41 0.59 0.59 0.55 Y₂O₃ 4.96 4.93 4.50 4.80 4.84 3.25 La₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Cu₂O 1.57 0.80 0.00 0.00 0.00 0.00 MnO 0.00 0.00 0.00 0.00 0.00 0.00 MnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 3.43 3.59 3.99 3.37 3.32 3.64 MgO/CaO 1.05 1.12 1.12 1.61 1.61 2.19 CaO + MgO + 12.29 15.24 16.76 15.35 15.48 17.33 BaO + SrO BaO + SrO + ZnO 0.00 0.00 0.00 0.00 0.00 2.46 T_(L) (° C.) 1153 1167 1219 1226 1201 1235 T_(F) (° C.) 1336 1291 1289 1307 1299 1320 ΔT (° C.) 183 124 70 81 98 85 T_(m) (° C.) 1547 1447 1491 1501 1493 1519 Fiber Density 2.62 2.64 2.63 (g/cm³) Fiber Modulus 91.1 91.8 92.6 (GPa) Fiber Strength 5321 5243 5583 (MPa) Fiber Failure Strain (%) 5.8 5.7 6.03 Specific Fiber 3.5 3.5 3.6 Modulus (×10⁶ m) Specific Fiber 207.0 202.5 216.6 Strength (×10³ m) 106 107 108 109 110 111 SiO₂ 60.48 62.01 64.00 66.00 65.00 63.00 Al₂O₃ 17.67 16.98 16.09 15.21 15.16 16.02 CaO 4.95 4.76 4.51 4.26 3.62 3.83 MgO 10.64 10.22 9.68 9.14 10.83 11.45 BaO 0.00 0.00 0.00 0.00 0.00 0.00 SrO 0.00 0.00 0.00 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.04 0.04 0.04 0.04 0.04 0.04 K₂O 0.10 0.10 0.09 0.09 0.09 0.09 Li₂O 0.95 0.90 0.86 0.80 0.80 0.85 Fe₂O₃ 0.26 0.25 0.24 0.23 0.23 0.24 TiO₂ 0.56 0.54 0.51 0.48 0.48 0.50 Y₂O₃ 4.33 4.20 3.98 3.75 3.74 3.96 La₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Cu₂O 0.00 0.00 0.00 0.00 0.00 0.00 MnO 0.00 0.00 0.00 0.00 0.00 0.00 MnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.004 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 3.42 3.65 3.98 4.34 4.29 3.93 MgO/CaO 2.15 2.15 2.15 2.15 2.99 2.99 CaO + MgO + 15.60 14.99 14.19 13.40 14.46 15.29 BaO + SrO BaO + SrO + ZnO 0.00 0.00 0.00 0.00 0.00 0.00 T_(L) (° C.) 1232 1234 1282 1332 1329 1288 T_(F) (° C.) 1299 1321 1348 1383 1358 1329 ΔT (° C.) 67 87 66 51 29 41 T_(m) (° C.) 1499 1522 1558 1601 1567 1532 Fiber Density 2.63 2.61 2.58 2.56 2.57 2.60 (g/cm³) Fiber Modulus 93.1 92.6 91.7 89.2 90.8 92.7 (GPa) Fiber Strength 5357.0 5462 5456 (MPa) Fiber Failure Strain (%) 5.8 5.9 6.0 Specific Fiber 3.54 3.55 3.55 3.49 3.53 3.57 Modulus (×10⁶ m) Specific Fiber 203.8 209.5 211.5 Strength (×10³ m) 112 113 114 115 116 117 SiO₂ 61.00 60.43 62.00 64.00 65.00 63.50 Al₂O₃ 16.88 17.70 17.00 16.11 15.67 14.91 CaO 4.04 0.10 0.10 0.09 0.09 5.11 MgO 12.08 10.65 10.22 9.68 9.41 10.11 BaO 0.00 0.00 0.00 0.00 0.00 0.00 SrO 0.00 0.00 0.00 0.00 0.00 0.00 ZnO 0.00 4.90 4.70 4.46 4.33 0.00 Na₂O 0.04 0.04 0.04 0.04 0.04 0.03 K₂O 0.10 0.10 0.10 0.09 0.09 0.08 Li₂O 0.91 0.95 0.91 0.86 0.84 0.50 Fe₂O₃ 0.25 0.25 0.24 0.23 0.23 0.24 TiO₂ 0.52 0.56 0.54 0.51 0.49 0.50 Y₂O₃ 4.17 4.30 4.14 3.92 3.80 5.01 La₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Cu₂O 0.00 0.00 0.00 0.00 0.00 0.00 MnO 0.00 0.00 0.00 0.00 0.00 0.00 MnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 3.61 3.41 3.65 3.97 4.15 4.26 MgO/CaO 2.99 102.58 102.58 102.58 102.58 1.98 CaO + MgO + 16.13 10.76 10.33 9.78 9.51 15.23 BaO + SrO BaO + SrO + ZnO 0.00 4.90 4.70 4.46 4.33 0.00 T_(L) (° C.) 1242 1296 1321 1361 1378 1330 T_(F) (° C.) 1301 1315 1338 1362 1381 1360 ΔT (° C.) 59 19 17 1 3 30 T_(m) (° C.) 1496 1516 1546 1577 1600 1572 Fiber Density 2.62 (g/cm³) Fiber Modulus 94.8 (GPa) Fiber Strength 5395 (MPa) Fiber Failure Strain (%) 5.7 Specific Fiber 3.62 Modulus (×10⁶ m) Specific Fiber 206.1 Strength (×10³ m) 118 119 120 121 122 123 SiO₂ 64.01 62.50 64.01 62.49 64.00 62.51 Al₂O₃ 13.57 16.93 17.34 16.70 17.37 16.93 CaO 5.34 2.41 0.09 1.30 0.09 4.70 MgO 10.55 9.10 9.28 10.49 9.28 10.20 BaO 0.00 0.00 0.00 3.05 3.20 0.00 SrO 0.00 3.04 3.23 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.03 0.03 0.03 0.03 0.03 0.03 K₂O 0.08 0.09 0.09 0.09 0.09 0.10 Li₂O 0.51 0.55 0.57 0.53 0.56 0.60 Fe₂O₃ 0.22 0.26 0.26 0.25 0.26 0.26 TiO₂ 0.46 0.58 0.60 0.58 0.60 0.58 Y₂O₃ 5.23 4.51 4.51 4.49 4.51 4.09 La₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Cu₂O 0.00 0.00 0.00 0.00 0.00 0.00 MnO 0.00 0.00 0.00 0.00 0.00 0.00 MnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 4.72 3.69 3.69 3.74 3.68 3.69 MgO/CaO 1.98 3.78 104.76 8.09 104.83 2.17 CaO + MgO + 15.90 14.55 12.60 14.84 12.57 14.90 BaO + SrO BaO + SrO + ZnO 0.00 3.04 3.23 3.05 3.20 0.00 T_(L) (° C.) 1352 1317 1348 1327 1347 1290 T_(F) (° C.) 1347 1381 1415 1378 1428 1350 ΔT (° C.) −5 64 67 51 81 60 T_(m) (° C.) 1552 1590 1633 1587 1648 1553 Fiber Density 2.611 2.5728 (g/cm³) Fiber Modulus 90.5 89.99 (GPa) Fiber Strength (MPa) Fiber Failure Strain (%) Specific Fiber 3.46 3.50 Modulus (×10⁶ m) Specific Fiber Strength (×10³ m) 124 125 126 127 128 129 SiO₂ 62.25 62.39 62.31 62.01 64.00 66.00 Al₂O₃ 16.72 16.63 16.85 16.98 16.09 15.21 CaO 4.78 5.01 4.97 4.76 4.51 4.26 MgO 10.20 10.01 9.93 10.22 9.68 9.14 BaO 0.00 0.00 0.00 0.00 0.00 0.00 SrO 0.00 0.00 0.00 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.03 0.03 0.03 0.04 0.04 0.04 K₂O 0.09 0.09 0.09 0.10 0.09 0.09 Li₂O 0.60 0.50 0.50 0.90 0.86 0.80 Fe₂O₃ 0.26 0.26 0.26 0.25 0.24 0.23 TiO₂ 0.57 0.58 0.59 0.54 0.50 0.48 Y₂O₃ 4.49 4.50 4.46 0.00 0.00 0.00 La₂O₃ 0.00 0.00 0.00 4.20 3.98 3.75 Cu₂O 0.00 0.00 0.00 0.00 0.00 0.00 MnO 0.00 0.00 0.00 0.00 0.00 0.00 MnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 3.72 3.75 3.70 3.65 3.98 4.34 MgO/CaO 2.13 2.00 2.00 2.15 2.15 2.15 CaO + MgO + 14.98 15.01 14.90 14.99 14.19 13.40 BaO + SrO BaO + SrO + ZnO 0.00 0.00 0.00 0.00 0.00 0.00 T_(L) (° C.) 1288 1292 1292 1234 1283 1338 T_(F) (° C.) 1339 1348 1346 1321 1363 1386 ΔT (° C.) 51 56 54 87 80 48 T_(m) (° C.) 1539 1550 1548 1527 1579 1608 Fiber Density (g/cm³) Fiber Modulus (GPa) Fiber Strength 5365 (MPa) Fiber Failure Strain (%) Specific Fiber Modulus (×10⁶ m) Specific Fiber Strength (×10³ m) 130 131 132 133 134 135 SiO₂ 65.00 63.00 61.00 60.43 62.00 64.00 Al₂O₃ 15.16 16.02 16.88 17.70 17.00 16.11 CaO 3.62 3.83 4.04 0.10 0.10 0.09 MgO 10.83 11.45 12.08 10.65 10.22 9.68 BaO 0.00 0.00 0.00 0.00 0.00 0.00 SrO 0.00 0.00 0.00 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 4.90 4.70 4.46 Na₂O 0.04 0.04 0.04 0.04 0.04 0.04 K₂O 0.09 0.09 0.10 0.10 0.10 0.09 Li₂O 0.80 0.85 0.90 0.95 0.90 0.86 Fe₂O₃ 0.23 0.24 0.25 0.25 0.24 0.23 TiO₂ 0.48 0.50 0.52 0.56 0.54 0.50 Y₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 3.74 3.96 4.18 4.31 4.14 3.92 Cu₂O 0.00 0.00 0.00 0.00 0.00 0.00 MnO 0.00 0.00 0.00 0.00 0.00 0.00 MnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 4.29 3.93 3.61 3.41 3.65 3.97 MgO/CaO 2.99 2.99 2.99 102.58 102.58 102.58 CaO + MgO + 14.46 15.29 16.13 10.76 10.33 9.78 BaO + SrO BaO + SrO + ZnO 0.00 0.00 0.00 4.90 4.70 4.46 T_(L) (° C.) 1313 1263 1259 1307 1315 1352 T_(F) (° C.) 1359 1325 1298 1324 1348 1380 ΔT (° C.) 46 62 39 17 33 28 T_(m) (° C.) 1574 1532 1496 1530 1563 1606 Fiber Density (g/cm³) Fiber Modulus (GPa) Fiber Strength 5355 (MPa) Fiber Failure Strain (%) Specific Fiber Modulus (×10⁶ m) Specific Fiber Strength (×10³ m) 136 137 138 139 140 141 SiO₂ 65.00 61.42 61.02 60.85 62.50 62.49 Al₂O₃ 15.67 17.85 17.80 17.62 16.93 16.70 CaO 0.09 5.42 6.00 5.64 2.41 1.30 MgO 9.41 8.81 8.22 9.18 9.10 10.49 BaO 0.00 0.00 0.00 0.00 0.00 3.05 SrO 0.00 0.00 0.00 0.00 3.04 0.00 ZnO 4.33 0.00 0.00 0.00 0.00 0.00 Na₂O 0.04 0.04 0.04 0.05 0.03 0.03 K₂O 0.09 0.11 0.11 0.10 0.09 0.09 Li₂O 0.84 0.96 0.93 1.00 0.55 0.53 Fe₂O₃ 0.23 0.37 0.38 0.37 0.26 0.25 TiO₂ 0.49 0.56 0.57 0.55 0.58 0.58 Y₂O₃ 0.00 4.45 4.94 4.64 4.51 4.49 La₂O₃ 3.80 0.00 0.00 0.00 0.00 0.00 Cu₂O 0.00 0.00 0.00 0.00 0.00 0.00 MnO 0.00 0.00 0.00 0.00 0.00 0.00 MnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 4.15 3.44 3.43 3.45 3.69 3.74 MgO/CaO 102.58 1.63 1.37 1.63 3.78 8.09 CaO + MgO + 9.51 14.23 14.21 14.82 14.55 14.84 BaO + SrO BaO + SrO + ZnO 4.33 0.00 0.00 0.00 3.04 3.05 T_(L) (° C.) 1371 1188 1185 1188 1317 1327 T_(F) (° C.) 1398 1319 1320 1307 1381 1378 ΔT (° C.) 27 131 135 119 64 51 T_(m) (° C.) 1625 1522 1521 1508 1590 1587 Fiber Density 2.61 2.62 2.62 2.61 (g/cm³) Fiber Modulus 92.3 91.9 92.0 90.5 (GPa) Fiber Strength 5490 5467 5492 (MPa) Fiber Failure Strain (%) 5.9 5.9 6.0 Specific Fiber 3.6 3.6 3.6 3.46 Modulus (×10⁶ m) Specific Fiber 215.0 213.2 214.2 Strength (×10³ m) 142 143 144 145 146 147 SiO₂ 64.01 64.00 61.28 61.28 60.18 60.18 Al₂O₃ 17.34 17.37 17.87 17.87 16.77 16.77 CaO 0.09 0.09 6.01 6.01 7.18 7.18 MgO 9.28 9.28 6.29 6.29 8.05 8.05 BaO 0.00 3.20 0.00 0.00 0.00 0.00 SrO 3.23 0.00 0.00 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.03 0.03 0.04 0.04 0.04 0.04 K₂O 0.09 0.09 0.11 0.11 0.10 0.10 Li₂O 0.57 0.56 0.93 0.93 1.01 1.01 Fe₂O₃ 0.26 0.26 0.38 0.38 0.37 0.37 TiO₂ 0.60 0.60 2.13 0.56 1.36 0.56 Y₂O₃ 4.51 4.51 4.96 4.96 4.93 4.93 La₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Cu₂O 0.00 0.00 0.00 1.57 0.00 0.80 MnO 0.00 0.00 0.00 0.00 0.00 0.00 MnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 3.69 3.68 3.43 3.43 3.59 3.59 MgO/CaO 104.76 104.83 1.05 1.05 1.12 1.12 CaO + MgO + 12.60 12.57 12.29 12.29 15.24 15.24 BaO + SrO BaO + SrO + ZnO 3.23 3.20 0.00 0.00 0.00 0.00 T_(L) (° C.) 1348 1347 1208 1153 1154 1167 T_(F) (° C.) 1415 1428 1338 1336 1294 1291 ΔT (° C.) 67 81 130 183 140 124 T_(m) (° C.) 1633 1648 1549 1547 1493 1447 Fiber Density 2.57 2.61 2.62 (g/cm³) Fiber Modulus 89.99 90.0 91.1 (GPa) Fiber Strength 5321 (MPa) Fiber Failure Strain (%) 5.8 Specific Fiber 3.50 3.5 3.5 Modulus (×10⁶ m) Specific Fiber 0.0 207.0 Strength (×10³ m) 148 149 150 151 152 153 SiO₂ 60.83 61.00 60.12 59.78 60.07 64.01 Al₂O₃ 15.23 16.75 17.84 17.99 17.52 13.57 CaO 7.90 4.67 5.88 5.93 5.92 5.34 MgO 8.86 10.20 9.47 9.55 9.63 10.55 BaO 0.00 0.00 0.00 0.00 0.00 0.00 SrO 0.00 2.46 0.00 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.04 0.04 0.04 0.04 0.04 0.03 K₂O 0.09 0.10 0.10 0.10 0.10 0.08 Li₂O 0.77 0.72 0.77 0.78 0.91 0.51 Fe₂O₃ 0.37 0.25 0.39 0.40 0.37 0.22 TiO₂ 1.41 0.55 0.59 0.59 0.56 0.46 Y₂O₃ 4.50 3.25 4.80 4.84 4.87 5.23 La₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Cu₂O 0.00 0.00 0.00 0.00 0.00 0.00 MnO 0.00 0.00 0.00 0.00 0.00 0.00 MnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 3.99 3.64 3.37 3.32 3.43 4.72 MgO/CaO 1.12 2.19 1.61 1.61 1.63 1.98 CaO + MgO + 16.76 17.33 15.35 15.48 15.55 15.90 BaO + SrO BaO + SrO + ZnO 0.00 2.46 0.00 0.00 0.00 0.00 T_(L) (° C.) 1219 1235 1226 1201 1200 1352 T_(F) (° C.) 1289 1320 1307 1299 1297 1347 ΔT (° C.) 70 85 81 98 97 −5 T_(m) (° C.) 1491 1519 1501 1493 1494 1552 Fiber Density 2.64 2.63 2.63 2.62 (g/cm³) Fiber Modulus 91.8 92.6 92.8 85.2 (GPa) Fiber Strength 5243 5583 5340 (MPa) Fiber Failure Strain (%) 5.7 6.03 5.8 Specific Fiber 3.5 3.6 3.6 Modulus (×10⁶ m) Specific Fiber 202.5 216.6 207.0 Strength (×10³ m) 154 155 156 157 158 159 SiO₂ 60.61 58.73 59.81 62.19 64.78 63.74 Al₂O₃ 15.26 14.78 15.06 15.66 16.31 16.05 CaO 7.01 4.75 0.06 0.03 0.03 0.03 MgO 5.49 5.29 6.07 2.38 2.48 2.44 BaO 0.00 0.00 0.00 0.00 0.00 0.00 SrO 0.00 0.00 0.00 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.04 0.04 0.04 0.04 0.04 0.04 K₂O 0.09 0.09 0.08 0.09 0.09 0.09 Li₂O 0.83 0.81 0.82 0.86 0.89 0.88 Fe₂O₃ 0.22 0.21 0.21 0.21 0.22 0.22 TiO₂ 2.00 7.11 6.50 6.76 7.04 6.93 Y₂O₃ 3.89 3.77 3.84 4.00 0.00 1.61 La₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Cu₂O 0.00 0.00 0.00 0.00 0.00 0.00 MnO 0.00 0.00 0.00 0.00 0.00 0.00 MnO₂ 4.55 4.41 7.49 7.79 8.12 7.99 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 3.97 3.97 3.97 3.97 3.97 3.97 MgO/CaO 0.78 1.11 99.34 86.24 86.24 86.24 CaO + MgO + 12.50 10.05 6.14 2.41 2.51 2.47 BaO + SrO BaO + SrO + ZnO 0.00 0.00 0.00 0.00 0.00 0.00 T_(L) (° C.) 1232 1350 1342 1356 1339 1347 T_(F) (° C.) 1362 1341 1321 1405 1444 1428 ΔT (° C.) 130 −9 −21 49 105 81 T_(m) (° C.) 1600 1579 1538 1645 1694 1677 Fiber Density 2.62 2.63 2.58 2.50 2.53 (g/cm³) Fiber Modulus 85.4 88.9 85.4 82.9 83.9 (GPa) Fiber Strength (MPa) Fiber Failure Strain (%) Specific Fiber Modulus (×10⁶ m) Specific Fiber Strength (×10³ m) 160 161 162 163 SiO₂ 63.40 69.97 63.25 60.85 Al₂O₃ 14.65 16.98 22.00 15.16 CaO 0.03 2.11 0.06 1.52 MgO 2.78 3.82 6.77 0.05 BaO 0.00 0.00 0.00 0.00 SrO 0.00 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 0.00 Na₂O 0.02 0.03 0.02 0.04 K₂O 0.07 0.09 0.11 0.09 Li₂O 0.00 0.54 0.00 0.79 Fe₂O₃ 0.23 0.25 0.34 0.21 TiO₂ 7.89 3.40 5.33 8.29 Y₂O₃ 1.83 0.94 0.00 5.07 La₂O₃ 0.00 0.00 0.00 0.00 Cu₂O 0.00 0.00 0.00 0.00 MnO 0.00 0.00 2.11 7.95 MnO₂ 9.11 1.86 0.00 0.00 B₂O₃ 0.00 0.00 0.00 0.00 SO₃ 0.00 0.00 0.00 0.00 TOTAL 100.00 100.00 100.00 100.00 SiO₂/Al₂O₃ 4.33 4.12 2.87 4.01 MgO/CaO 110.30 1.81 109.95 0.03 CaO + MgO + 2.81 5.94 6.83 1.56 BaO + SrO BaO + SrO + ZnO 0.00 0.00 0.00 0.00 T_(L) (° C.) 1456 1387 1389 1392 T_(F) (° C.) 1450 1547 1426 1385 ΔT (° C.) −6 160 37 −7 T_(m) (° C.) 1684 1812 1646 1626 Fiber Density 2.44 2.55 (g/cm³) Fiber Modulus 83.3 83.9 (GPa) Fiber Strength (MPa) Fiber Failure Strain (%) Specific Fiber Modulus (×10⁶ m) Specific Fiber Strength (×10³ m)

Desirable characteristics that can be exhibited by various but not necessarily all embodiments of the present invention can include, but are not limited to, the following: the provision of glass fibers, fiber glass strands, glass fiber fabrics, composites, and related products having a relatively low density; the provision of glass fibers, fiber glass strands, glass fiber fabrics, composites, and laminates having a relatively high tensile strength; the provision of glass fibers, fiber glass strands, glass fiber fabrics, composites, and related products having a relatively low density; the provision of glass fibers, fiber glass strands, glass fiber fabrics, composites, and laminates having a relatively high modulus; the provision of glass fibers, fiber glass strands, glass fiber fabrics, composites, and laminates having a relatively high elongation; the provision of glass fibers, fiber glass strands, glass fiber fabrics, prepregs, and other products useful for reinforcement applications; and others.

It is to be understood that the present description illustrates aspects of the invention relevant to a clear understanding of the invention. Certain aspects of the invention that would be apparent to those of ordinary skill in the art and that, therefore, would not facilitate a better understanding of the invention have not been presented in order to simplify the present description. Although the present invention has been described in connection with certain embodiments, the present invention is not limited to the particular embodiments disclosed, but is intended to cover modifications that are within the spirit and scope of the invention. 

What is claimed is:
 1. A glass composition suitable for fiber forming comprising: SiO₂ from about 51 to about 70 weight percent; Al₂O₃ from about 12.5 to about 22 weight percent; CaO from 0 to about 20 weight percent; MgO from 0 to about 11 weight percent; Fe₂O₃ from about 0.2 to about 1 weight percent; RE₂O₃ about 0.05 or greater weight percent; BaO from 0 to about 4 weight percent; SrO from 0 to about 4 weight percent; and ZnO from 0 to about 5.5 weight percent;

wherein the sum of BaO+SrO+ZnO is greater than 2 weight percent.
 2. The glass composition of claim 1, wherein the sum of BaO+SrO+ZnO is greater than 3 weight percent.
 3. The glass composition of claim 1, wherein BaO is present in an amount greater than 2 weight percent.
 4. The glass composition of claim 1, wherein SrO is present in an amount greater than 2 weight percent.
 5. The glass composition of claim 1, wherein ZnO is present in an amount greater than 2 weight percent.
 6. The glass composition of claim 1, further comprising less than 1.5 weight percent Na₂O+K₂O+Li₂O.
 7. The glass composition of claim 1, further comprising from 0 to about 1 weight percent B₂O₃.
 8. A glass composition suitable for fiber forming comprising: SiO₂ from about 51 to about 65 weight percent; Al₂O₃ from about 12.5 to about 22 weight percent; CaO from 0 to about 20 weight percent; MgO from 0 to about 12 weight percent; Fe₂O₃ from about 0.2 to about 1 weight percent; RE₂O₃ greater than 2 weight percent, wherein RE₂O₃ comprises La₂O₃ in an amount greater than 2 weight percent; and at least one additional feature selected from the group consisting of: CaO is present in an amount less than 2 weight percent; a ratio of MgO content to CaO content (MgO/CaO) less than 1; and a ratio of SiO₂ content to Al₂O₃ content (SiO₂/Al₂O₃) greater than
 4.


9. The glass composition of claim 8, wherein the composition comprises La₂O₃ in an amount greater than 3 weight percent.
 10. The glass composition of claim 8, wherein MgO is present in an amount greater than 6 weight percent, and the additional feature comprises CaO in an amount less than 1.5 weight percent.
 11. The glass composition of claim 8, wherein the additional feature comprises the SiO₂/Al₂O₃ ratio in an amount greater than 4.2.
 12. The glass composition of claim 8, further comprising less than 1.5 weight percent Na₂O+K₂O+Li₂O. 